1. PENGACUANAN SUNTIKAN (INJECTION MOULDING)

2. CONTOH PRODUK

3. PERHATIKAN RAJAH ASAS PROSES PENGACUANAN SUNTIKAN DAN JENIS JENIS MESIN PENGACUANAN SUNTIKAN

8. LANGKAH ASAS PENGACUANAN SUNTIKAN
PELEBURAN RESIN
PENYUNTIKAN RESIN YANG TELAH LEBUR KE DALAM ACUAN TERTUTUP
PENYEJUKAN RESIN DI DALAM ACUAN TERTUTUP
PEMBUKAAN ACUAN DAN PENGELUARAN (EJECTION) PLASTIK TERACUAN

9. CONVENTIONAL INJECTION MOULDING

10. PISTON TYPE PREPLASTIFYING

11. SCREW TYPE PREPLASTIFYING

12. RECIPROCATING SCREW INJECTION

13. SELALU DIGUNAKAN UNTUK TERMOPLASTIK ATAU TERMOSET TIDAK DIPERKUATKAN
BOLEH JUGA DIGUNAKAN UNTUK MENGHASILKAN KOMPOSIT DIPERKUATKAN GENTIAN PENDEK DAN UNTUK TERMOSET
PLASTIK YANG BIASA DIPROSES DENGAN TEKNIK INI IALAH PP, PA DAN PC

15. SLIDE SHOW
ON 100 PERCENT

16. KELEBIHAN PENGACUANAN SUNTIKAN
PRODUK BOLEH DIHASILKAN DENGAN PANTAS (KADAR PENGELUARAN TINGGI)
PENGELUARAN ISIPADU TINGGI ADALAH MUNGKIN
KOS BURUH YANG RENDAH PER UNIT MESIN
PRODUK TIDAK MEMERLUKAN ‘FINISHING’

17. PERMUKAAN, WARNA DAN ‘FINISHING’ YANG BERLAINAN BOLEH DIHASILKAN
PENGGUNAAN PELBAGAI PLASTIK DAPAT DILAKUKAN TANPA PERLU MENUKAR MESIN ATAU ACUAN
UNTUK KEBANYAKAN REKABENTUK, PROSES INI ADALAH PALING EKONOMIK UNTUK DIHASILKAN

18. KEKURANGAN PENGACUANAN SUNTIKAN
INDUSTRI PLASTIK MEMPUNYAI KEUNTUNGAN YANG RENDAH (LOW PROFIT MARGIN)
OPERASI TIGA SHIFT PERLU UNTUK BERSAING
KOS ACUAN SANGAT TINGGI
MESIN DAN PERALATANNYA MAHAL
KAWALAN PROSES MUNGKIN TIDAK BEGITU BAIK
PERALATAN TIDAK KONSISTEN SEMASA BEROPERASI
KUALITI MUNGKIN AGAK SUKAR DITENTUKAN SERTA MERTA

19. PROSES ASAS
LEBURAN ATAU ‘PLASTICISED’ PLASTIK DI SUNTIK ATAU DIPAKSA KE DALAM ACUAN DI MANA IA DI SIMPAN SEHINGGA DIKELUARKAN DALAM KEADAAN PEPEJAL DAN MENYERUPAI KAVITI ACUAN YANG DIGUNAKAN

20. ACUAN MUNGKIN TERDIRI DARI SATU KAVITI ATAU BANYAK KAVITI (MULTI CAVITY) YANG BERBENTUK SAMA ATAU BERLAINAN, SETIAP SATU DISAMBUNGKAN DENGAN ‘CHANNEL’ ALIRAN ATAU ‘RUNNERS’ YANG MENGARAHKAN LEBURAN KE DALAM SETIAP KAVITI
PROSES INI ADALAH SALAH SATU KAEDAH YANG PALING EKONOMIK UNTUK PENGELUARAN PRODUK SECARA BESAR-BESARAN

21. SPRU, “RUNNER”, PINTU DAN KAVITI

22. TERDAPAT EMPAT (4) OPERASI ASAS:
MENINGKATKAN SUHU PLASTIK KE SUATU TAHAP IA AKAN MENGALIR DI BAWAH TEKANAN – PEMANASAN DAN PENCAMPURAN SECARA SERENTAK – MENGHASILKAN LEBURAN YANG SERAGAM SUHU DAN KELIKATAN. KESELURUHAN PROSES INI DIPANGGIL ‘PLASTICATION’ ATAU ‘PLASTICIZING’

23. MEMBOLEHKAN LEBURAN PLASTIK MEMBEKU DALAM ACUAN YANG DITUTUP
MEMBOLEHKAN LEBURAN PLASTIK MEMBEKU DALAM ACUAN YANG DITUTUP. LEBURAN PLASTIK DARI SILINDER SUNTIKAN DIPINDAHKAN MELALUI BEBERAPA ‘CHANNEL’ ALIRAN (RUNNER) KE DALAM KAVITI
PENYEJUKAN
MEMBUKA ACUAN UNTUK MENOLAK KELUAR (EJECTION) PLASTIK YANG TELAH MENJADI PEPEJAL DENGAN CARA MENGELUARKAN HABA DARI LEBURAN

24. OPERASI TADI AKAN MENENTUKAN PRODUKTIVITI KERANA KELAJUAN PENGELUARAN BERGANTUNG PADA BERAPA CEPAT PLASTIK DILEBURKAN, BERAPA CEPAT IA BOLEH DISUNTIK DAN BERAPA LAMA MASA UNTUK MENYEJUKKANNYA DALAM ACUAN – PUSINGAN PENYUNTIKAN

25. KOMPONEN ASAS UNTUK SISTEM PENGACUANAN SUNTIKAN:
PENYEBATIAN
PENGERINGAN
PENYUAPAN
PEMETERAN
PLASTICATION (PELEBURAN)
PENYUNTIKAN
PENYEJUKAN
PENOLAKAN KELUAR (EJECTION)

26. URUTAN PERGERAKAN MEKANIKAL UMUM SEMASA PEMPROSESAN:
PENGAPIT (ACUAN) DITUTUP
RAM PENYUNTIKAN BERGERAK KE DEPAN UNTUK MENYUNTIK LEBURAN
SKRU MENGEPAM KE BELAKANG APABILA LEBURAN SEJUK DALAM ACUAN
SKRU BERHENTI BERPUTAR DAN PENGAPIT DIBUKA
PLASTIK TERACUAN DITOLAK KELUAR DARI ACUAN

27. Resin feed into the barrel
Shot accumulates here

28. CAVITY GETS FILLED
SCREW MOVES FORWARD

29. PRESSURE IS MAINTAINED IN CAVITY
COOLING LINES
PRESSURE IS MAINTAINED IN CAVITY

30. MOULD IS OPENED

31. UNTUK MENDAPATKAN KEPUTUSAN YANG OPTIMUM BAGI SESUATU PLASTIK DAN ACUAN :
SUHU PELEBURAN
TEKANAN PENYUNTIKAN (INJECTION PRESSURE)
KELAJUAN PENGISIAN ACUAN (INJECTION SPEED)

32. SUHU PELEBURAN

33. PLASTIK BERBEZA DARI SEGI KELIKATAN (PENGALIRAN – EASE OF FLOW) DAN MASALAH INI MENJADI LEBIH RUMIT DENGAN ADANYA GRED YANG PELBAGAI
TAMBAHAN LAGI SIFAT PENGALIRAN PLASTIK ADALAH NON-NEWTONIAN (HUBUNGAN TIDAK LINEAR ANTARA TEKANAN DAN PENGALIRAN)
SIFAT PENGALIRAN TIDAK BOLEH DIWAKILI OLEH SATU NILAI SAHAJA

34. CONTOH KELIKATAN PLASTIK PADA SUHU BERBEZA
BAHAN
(NYLON)
KELIKATAN PADA 1,000 s-1
240˚C
260˚C
280˚C
300˚C 1 98 78 63 50 2
149
115 89 69 3
394
319
259
210

35. CONTOH KELIKATAN PLASTIK PADA KADAR RICIH BERBEZA
BAHAN
KELIKATAN PADA SUHU 280˚C
100s-1
1000s-1
10000s-1
100,000s-1 1
197 63 20 6 2
323 89 25 7 3
1220
259 55 12

36. DALAM KEBANYAKAN KES, PLASTIK ADALAH BERSIFAT PSEUDOPLASTIK IAITU MEREKA MENJADI KURANG LIKAT (SENANG MENGALIR) BILA DIGERAKKAN DENGAN CEPAT
KELIKATAN BAHAN BERKURANG BILA KADAR RICIH DITINGKATKAN (PENGISIAN ACUAN LEBIH MUDAH)
MENINGKATKAN SUHU LEBURAN AKAN KURANGKAN TEKANAN PENYUNTIKAN YANG DIPERLUKAN PADA KADAR PENGALIRAN TERTENTU

37. SUHU PENGACUANAN BEBERAPA JENIS PLASTIK

38. TEKANAN PENYUNTIKAN

39. SEMASA PENGISIAN ACUAN, TEKANAN PENYUNTIKAN TINGGI PERLU UNTUK MENGEKALKAN KELAJUAN PENGISIAN ACUAN YG DIPERLUKAN
BILA ACUAN TELAH PENUH, TEKANAN TINGGI TIDAK LAGI DIPERLUKAN
MUNGKIN BOLEH GUNAKAN 2 PERINGKAT TEKANAN

40. (KELAJUAN PENGISIAN ACUAN)
KELAJUAN PENYUNTIKAN
(KELAJUAN PENGISIAN ACUAN)

41. BILA MENGACUANKAN PRODUK NIPIS, KELAJUAN TINGGI DIPERLUKAN UNTUK MEMENUHKAN ACUAN SEBELUM PEMBEKUAN BAHAN
UNTUK MENDAPATKAN PERMUKAAN YANG BAIK BAGI PRODUK TEBAL, SUNTIKAN PERLAHAN DIGUNAKAN
BAGI KEBANYAKAN MESIN, MASA UNTUK MENGISI ACUAN SELESAI DALAM MASA 1 SAAT

42. SAIZ MESIN
DARI BEBERAPA GRAM KEPADA BEBERAPA PAUN (ADA YANG MENCAPAI HINGGA 395 PAUN, KEKUATAN PENGAPIT 10,000 TAN)
‘MINIATURE INJECTION MOULDING MACHINE’ (RAJAH). TERDAPAT BANYAK CABARAN UNTUK PERKEMBANGAN PADA MASA DEPAN. KEPERLUAN UNTUK ACUAN MIKRO:
PEMANASAN DAN PENYEJUKAN YANG CANGGIH
VAKUM UNTUK KAVITI
PENGESAN YANG KHUSUS
PERALATAN DENGAN KETEPATAN TINGGI DIPERLUKAN

43. MINIATURE INJECTION MOULDING MACHINE

45. MESIN PENYUNTIKAN YANG SANGAT BESAR (LIHAT RAJAH)
MESIN PENYUNTIKAN YANG SANGAT BESAR (LIHAT RAJAH). DISEBABKAN OLEH KEPERLUAN INDUSTRI AUTOMOTIF, PERKAKASAN & BANGUNAN, PEMBINAAN DAN LAIN-LAIN. PENGGUNAAN MASA KINI/DEPAN:
BADAN KERETA/PANEL
ALAT PERKAKASAN (PETI SEJUK DAN MESIN BASUH)
BADAN BOT
KOLAM RENANG
MESIN YANG AGAK BESAR:
HUSKEY E8000
KEKUATAN PENGAPIT (CLAMP FORCE) 8000 TAN
SAIZ PLATEN: 19 X 16 X 13 KAKI
BERAT SUNTIKAN: 20 – 145 PAUN

46. MESIN PENGACUANAN SUNTIKAN YANG BESAR

48. KADAR PENYUNTIKAN KADAR PENYUNTIKAN BOLEH DIPELBAGAIKAN
LEBIH PANTAS MEMBOLEHKAN PENGACUANAN BENDA NIPIS DAN KURANGKAN MASA
KEUPAYAAN KADAR PENYUNTIKAN BERGANTUNG KEPADA SAIZ MESIN – LEBIH BESAR MESIN LEBIH TINGGI KADAR PENYUNTIKAN
KEUPAYAAN KADAR PENYUNTIKAN BERKADAR TERUS DENGAN PAM HIDROLIK. KADAR PENGALIRAN HIDROLIK DALAM GELEN PER MINIT MENENTUKAN KADAR PENYUNTIKAN
TEKANAN HIDROLIK MENENTUKAN TEKANAN SUNTIKAN