1. Ta-C Hard coating www.iiwit.com

2. Contents 1.Company Technology 2. PCB Drills 3. PCB Routers 4. Endmills/Insert 5. Molds

3. Company Technology Established in May 1999, Nanofilm Technologies International Pte Ltd is an internationally recognized authority in the field of Filtered Cathodic Vacuum Arc (FCVA) Technology. Our FCVA coating technology represents a significant advancement in thin film deposition, and is the result of 7 years ground-breaking work by a team of researchers led by Associate Professor Dr. Shi Xu, the Chairman and co-founder of Nanofilm. Filtered Cathodic Vacuum Arc (FCVA) Technology Our FCVA Technology has received numerous academic awards, including the prestigious Singapore Innovation Award & National Technology Award conferred by the National Science & Technology Board of Singapore. Nanofilm has a portfolio of patents covering various areas of FCVA Technology and its applications.patents

4. Company Technology Arc-evaporation deposition is normally used to apply wear-resistant coatings to machine tools. However, the substantial distribution of macroparticles associated with this process limits the film quality. To solve this problem, Nanofilm Technologies International Pte Ltd has developed a revolutionary new version of FCVA deposition technology. Our patented technology can produce high quality Tetrahedral Amorphous Carbon (ta-C) coatings to satisfy even the most stringent requirements.ta-C During deposition, the surface temperature of the substrate is generally below 70 °C, which makes coating on plastic possible too.

5. Film Qualities Company name www.iiwitcom Film by Competitor's Cathodic Arc Technology *Under optical microscope (X200) Film by Nanofilm's Double Bend FCVA Technology *Under optical microscope (X200)

6. Classification Company name www.iiwitcom Sp3 bound Sp2 bound FCVA technology can make The ta-C contains up to 88% of sp3 bonds

7. PCB Drills - Super high hardness (3000~6000HB). - Wear and scratch resistance. - Excellent adhesion to surface. - Extremely smooth coating surface. - Better release performance. - Corrosion resistance. - Diameter of plated through hole is getting smaller - The number of through holes is getting higher per square meter - Prolong the lifespan by 2 times on the flexible board, 4 times on the BAG board - Obviously avoid the fracture (0.1mm PCB drills) - Excellent smooth surface of the through hole - Excellent CPK Performance - Longer tools maintenance cycle - Less Manufacturing Downtime. - Lower production cost What is ta-C film provide: What are customer benefits :

8. PCB Drills Drilling of Double Sided Cu Clad/Fiber Reinforced Substrate: PCB Drills Workpiece : 2 layers, ½oz Cu, 0.8mm thickness, BT, 1 lot 30 panels Tool : Carbide drill bit with 0.3mm diameter Spindle Speed : 60,000 rpm Process : Continuous drilling without repointing CTQ : Top flute width Rejection Criteria : 30% wear of top flute Conclusion: ta-C Coating Extends Lifespan of Drill Bits by 3 Folds

9. PCB Drills Drilling of 16 Layers Cu Clad/Fiber Reinforced Substrate: PCB Drills Workpiece : 16 layers, ½ oz Cu, 2.1mm thickness, high Tg FR4,1 lot 30 panels Tool : Carbide drill bit with 0.3mm diameter Spindle Speed : 120,000 rpm Process : Repoint every 2000 hits CTQ : Nailheading, burr and roughness Conclusion: ta-C Coating Achieves Cost Reduction of 41%

10. PCB Routers Test condition: - FR4 board with thickness of 0.6mm - 2 layer per stack - Spindle speed : 35 Krpm - Feeding rate : 0.7 m/minutes - Board width : 60±0.1 mm PCB Routers Conclusion: After 16m routering with uncoated router, the PCB board is out of specification. After 56m routering with ta-C coated router, the PCB board is out of specification.

11. Endmills - Super high hardness (3000~6000HB). - Wear and scratch resistance. - Excellent adhesion to surface. - Extremely smooth coating surface. - Better release performance. - Corrosion resistance. - Excellent performance in some sticky metals cutting (anti-sticky) - Excellent smooth surface after cutting - Excellent CPK performance - Higher cutting speed - Longer tools maintenance cycle - Less Manufacturing Downtime. - Lower production cost - Longer tool life What is ta-C film provide: What are customer benefits :

12. Endmills Endmills Test: Workpiece : Aluminum block Tool : Carbide end mill with 8 mm diameter Roatating speed: 1400rpm Feeding speed: 100mm/min Milling depth: 5 mm Process: Continuous milling without repointing CTQ: Top flute wear

13. Endmills Result: - After 2 hours of milling with uncoated Carbide End Mill With Uncoated End MillSurface Morphology of Al Block - After 4 hours of milling with ta-C coated Carbide End Mill With Ta-C coated End MillSurface Morphology of Al Block Severe wear is observed Texture line on surface is damaged Surface becomes rough Minimum wear Texture line on surface remains intact Surface is still smooth

14. Endmills Conclusion: ta-C coating helps to prolong lifespan of end mills significantly and improve finished milling surface ta-C coated cutters are capable of performing dry cutting operations.

15. Insert www.iiwitcom Insert: - Al Cutting performance on Insert

16. Mold- Plastic Injection - Super high hardness. - Wear and scratch resistance. - Extremely smooth coating surface. - Better release performance. - Corrosion resistance. - Longer tool life - Excellent anti-sticky performance - Excellent anti-rust performance - Longer mold maintenance cycle - Better plastic parts quality - Lower production cost - Mirror surface maintained What is ta-C film provide: What are customer benefits : Example. Mould Material: 8407 Plastic Material: PVC Requirement: Anti-corrosion Life span without coating ： 120K Life span after coating: 500K Molding Speed: 3pc/minutes

17. Mold- Plastic Injection Example. Mould Material: 8407 Plastic Material: PA + 45% Glass Fiber Requirement: Anti-corrosion; Anti-wear Life span without coating ： 100K Life span after coating: 500K Molding Speed: 3pc/minutes Mould Material: 8407 Plastic Material: PC + 35% Glass Fiber Requirement: Anti-corrosion; Anti-wear; Mirror surface Life span without coating ： 0-100K; Frequent re-polishing required for heavy scratch Life span after coating: 400K; No re-polishing required Molding Speed: 3pc/minutes

18. Mold- Glass Lens / CD - DVD - Super high hardness. - Wear and scratch resistance. - Extremely smooth coating surface. - Better release performance. - Corrosion resistance. - Longer tool life - Excellent anti-sticky performance - Excellent anti-rust performance - Longer mold maintenance cycle - Better plastic parts quality - Lower production cost - Mirror surface maintained What is ta-C film provide: What are customer benefits : Glass Lens MoldCD / DVD Mold

19. Mold- Glass Lens / CD - DVD  TAC-ON coated mirror molds experience lesser wear  Better adhesion strength on mold surface as compared to conventional DLC coating.  Mold release and fillings are easier and smoother due to the low surface energy of TAC-ON coated mirror mold. Advantages of ta-C coating on mold :  Film thickness is low yet harder  Surface Energy is small and contact angle is high  Excellent adhesion  Excellent Anti-Sticking properties  Low wear rate  Lower-coefficient of friction  Achieve better easy release property

20. www.iiwit.com