Presented by: Chandra bhan prajapati 2008AMD2934.

Slides:

Advertisements

Similar presentations

2.008 Metal Casting.

Advertisements

UNIT -6 Rapid Tooling.

CASTING TECHNIQUES FOR SINGLE CRYSTAL GROWING (S.C.G.)

Manufacturing Processes

Ken YoussefiMechanical Engineering Dept., SJSU 1 Fundamentals of Casting Casting, one of the oldest manufacturing processes, dates back to 4000 B.C. when.

Chapter 13: Forming Processes. Forming Processes Forming Processes: the choice of manufacturing process depends on the size, shape and quality of the.

Type Of Casting Process

ME 330 Manufacturing Processes CASTING PROCESSES (cont.)

6-1 Chapter 6 Overview b Four major alloy groups most common: Aluminum, magnesium, zinc and ZA Aluminum, magnesium, zinc and ZA b These alloys have a range.

Metal casting M.A.E.Saleh KSU– IE351.

Chapter 9IT 2081 Thermal Methods of Change of Form Chapter 9.

A SEMINAR REPORT ON INVESTMENT CASTING

Casting Processes Example Parts Requirements Terminology

Fundamentals of Metal Forming Chapter 18

MSE 440/540: Processing of Metallic Materials

Casting. Die Metal is injected into the mould under high pressure of Mpa.Generally good surface finish and good dimensional accuracy. Typical Thin-walled:

Permanent Mould Casting

MANUFACTURING TECHNOLOGY

13.1 Introduction In expendable mold casting, a separate mold is produced for each casting Low production rate Quality control issues, such as dimensional.

Casting Workshop Technology

0 Casting since about 4000 BC… Ancient Greece; bronze statue casting circa 450BC Iron works in early Europe, e.g. cast iron cannons from England circa.

IE 337: Materials & Manufacturing Processes

The problem of foundry production is manufacture of billets and machine parts by pouring fused metal into a casting mould, whose cavity has the shape of.

Casting vs Fabrication $100,000 cumulative saving after 5 years Tooling payback by savings 1 year production.

ME 3351 Manufacturing Processes Tutorial 5 Eng. Ahmad Aljazea.

Reading: Kalpakjian pp

Selection Criteria Properties Availability Cost Manufacturability

Casting Mukul Gupta ID# M-L. Casting A manufacturing process used to solidify objects from their liquid form into various useful shapes by introducing.

AS Materials & Processes Design Section - Camera.

Non Ferrous Metals. Aluminum  Relatively new material  Requires little energy to produce 10 kwh for each pound  Ore is generally strip mined.

METAL CASTING PROCESSES 1.Permanent Mold Casting Processes ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e.

Working Metals Depending on the application, the process used to work a metal may vary. Common processes include: Casting Forging / Pressing Fabricating.

Chapter 13: Multiple-Use-Mold Casting Processes

Selection Criteria Properties Availability Cost Manufacturability

Beyond Stereolithography

Lecture 12 Different types of extrusion and their characteristics

METAL CASTING PROCESSES 1. Product Design Considerations ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e.

Topic 4 – Manufacturing Processes and Techniques Fall 2006.

Chapter 13 Multiple-Use-Mold Casting Processes (Part I) EIN 3390 Manufacturing Processes Summer A, 2012.

DESIGN CONSIDERATIONS CAREFUL CONTROL OF LARGE NUMBER OF VARIABLES NEEDED- CHARACTERISTICS OF METALS & ALLOYS CAST METHOD OF CASTING MOULD AND DIE MATERIALS.

Casting & Welding Engineering (IE 203) Second Year, Industrial Engineering Dept., Faculty of Engineering, Fayoum University Dr. Ahmed Salah Abou Taleb.

Manufacturing Processes

METAL CASTING Dipersiapkan oleh: MOERWISMADHI ST. MT

Metals All metals belong to one of these two groups. Ferrous metals are metals, which are mainly made of iron with small amounts of other metals or elements.

Special Casting Processes. Shell Casting Investment Casting Centrifugal Casting Die Casting Ceramic Mould CO2 Moulding.

Manufacturing Processes

METAL CASTING PROCESSES

Ceramic Mold Casting Similar to plaster mold casting except that mold is made of refractory ceramic material that can withstand higher temperatures than.

Introduction to nonferrous metal and alloys

1 CASTING DEFECTS Submitted to, A.R.Patel M.K.Patel Submitted by, Jaymin Panchal Subject : MP-II.

Casting Processes Dr Ajay Batish.

Engineering Materials and Processes Lecture 5 – Casting Process

Metal Casting - by MANIGANDAN.

a permanent mold casting process using pressure other than gravity

Manufacturing Processes

PATTERN MATERIAL REQUIREMENTS OF A GOOD PATTERN MATERIAL: IT SHOULD BE

Chapter 12 Metal Casting: Design, Materials, and Economics

NET SHAPE PROCESS SUBMITTED BY: TRUPTI RANJAN BISWAL

Manufacturing Processes

PLASTIC FORMING PROCRSSES

METAL CASTING PROCESSES

Metal processes.

FUNDAMENTALS OF METAL CASTING

Chapter 2 Material and Manufacturing Properties

4.5 Permanent-Mold Casting Processes

Selection Criteria Properties Availability Cost

Permanent Mold Casting

Manufacturing Technology 1 CUPE219 Lecturer details L. Chidzuu Office: E3 Contact: Metal casting process Permanent.

Presentation transcript:

Presented by: Chandra bhan prajapati 2008AMD2934

The casting process is subdivided into two distinct subgroups: 1 - Expendable mold casting (sand, plastic, shell, and investment (lost-wax technique) mouldings.) 2 - Nonexpendable mold casting (permanent, die, centrifugal, and continuous casting). Classification of die casting: (a)Gravity Die Casting (also called permanent mould process) (b)Pressure Die Casting

Die Casting Process Flow (Image courtesy: wiki)

[Pressure-die casting] [ pressure die Casting Techniques] [Die cast Part of automobile] [Die casting Fence fittings] (Image courtesy: wiki)

(Hot Die Casting machine) (Image courtesy: wiki) There are two basic types of die casting machines: (1)hot-chamber machines (2) cold-chamber machines

cold-die-casting machine (Image courtesy: wiki)

Attribute/proc ess sandinvestmentGravity diePressure die Max. size Several tons Upto 20 kgUpto 50 kgUpto 8 kg Dim. tolerance>0.6 mm>0.1 mm>0.4 mm>.05 mm Surface finish>200 rms>60 rms>150 rms>30 rms Min. thickness>6 mm>1.5 mm>4.5 mm>0.8 mm Economic quantity Any no.>100>500>2500 Table : Capabilities of major casting processes

( Cooling Curve for casting) (Image courtesy: wiki) Chvorinov's rule: The local solidification time can be calculated using Chvorinov's rule, which is:

Structure: (Intermediate cooling rates from melt result in a dendritic microstructure. (Image courtesy: wiki)

Material Min. Thickness mm (in) Min. Draft Angle (º) Aluminum alloys 0.9 mm 0.5 Zinc alloys 0.6 mm 0.25 Copper alloys (Brass) 1.25 mm 0.7 Minimum wall thicknesses and minimum draft angles for die casting are :

Die casting materials: Zinc: the easiest alloy to cast; high ductility; high impact strength; easily plated; economical for small parts; promotes long die life. Aluminum: lightweight; high dimensional stability for complex shapes and thin walls;. Magnesium: the easiest alloy to machine; excellent strength- to-weight ratio; lightest alloy commonly die cast. Copper: high hardness; high corrosion resistance; highest mechanical properties of alloys die cast; excellent wear resistance.

MaterialSiliconCopper Tensile Strength MPa (ksi) Properties AA 380 (UNS A03800) 8.5 %3.5 % 324 (47) Fair easy to fill AA 384 (UNS A03840) 11 %4 % 331 (48) Easy to fill AA 386 (UNS A03860) 9.5 %0.6 % 317 (46) Good corrosion resistance AA 390 (UNS A03900) 17 %4.5 % 283 (41) Good wear resistance Common aluminum alloys for die casting are summarized as follows:

Advantages: Excellent dimensional accuracy Smooth cast surfaces (1 — 2.5 μm rms). Thinner walls can be cast Inserts can be cast-in (such as threaded inserts, heating elements ) Reduces or eliminates secondary machining operations. Rapid production rates. tensile strength as high as 415 MPa. Disadvantages: Casting weight must be between 30 grams and 10 kg Casting must be smaller than 600 mm High initial cost. Limited to high-fluidity metals. A certain amount of porosity is common. Thickest section should be less than 13 mm A large production volume is needed to make this an economical.

THANK YOU