METAL CASTING PROCESSES

Published byMerilyn Bishop Modified over 5 years ago

Similar presentations

Presentation on theme: "METAL CASTING PROCESSES"— Presentation transcript:

1 METAL CASTING PROCESSES
Sand Casting Expendable Mold Casting Processes Permanent Mold Casting Processes Foundry Practice In-class Assignment ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

2 Overview of Sand Casting
Most widely used casting process Nearly all alloys can be sand casted Castings range in size and production quantity A large sand casting weighing over 680 kg (1500 lb) for an air compressor frame (photo courtesy of Elkhart Foundry) ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

3 Sand Casting Production Sequence
Cavity formed by packing sand around a pattern Gating and riser system Core used for internal geometry New sand mold for each part ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

4 Types of Patterns Patterns slightly enlarged to account for shrinkage
Patterns made of wood, metal or plastic solid split match‑plate cope and drag ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

5 Core in Mold (a) core held in place in the mold cavity by chaplets
(b) possible chaplet design (c) casting with internal cavity ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

6 Molds & Sands Typical mix: 90% sand, 3% water, and 7% clay
Desirable Mold Properties Strength Permeability Thermal stability Collapsibility & reusability Foundry Sands Silica (SiO2) Small grain  better surface finish Large grain  more permeable Typical mix: 90% sand, 3% water, and 7% clay ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

7 Shell Molding ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

8 Shell Molding Disadvantages: Expensive metal pattern
Difficult to justify for small quantities Advantages of shell molding: Better surface finish Good dimensional accuracy ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

9 Vacuum Molding ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

10 Expanded Polystyrene Process (Lost Foam)
Advantages Pattern need not be removed Simplifies and speeds mold‑making Disadvantages A new pattern is needed for every casting Economic justification of the process Application Automotive engines ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

11 Investment Casting (Lost Wax Process)
©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

12 Investment Casting (Lost Wax Process)
A one‑piece compressor stator with 108 separate airfoils made by investment casting (photo courtesy of Howmet Corp.) ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

13 Permanent Mold Casting
(1) mold is preheated and coated (2) cores (if used) are inserted and mold is closed (3) molten metal is poured into the mold Application – automotive pistons ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

14 Low-Pressure Casting ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

15 Hot-Chamber Die Casting
Low melting‑point metals that do not chemically attack mechanical components Casting metals: zinc, tin and lead ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

16 Casting metals: aluminum, brass, and magnesium alloys
Cold Chamber Casting Casting metals: aluminum, brass, and magnesium alloys ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

17 Cold Chamber Die Casting Machine
Mold usually made of tool steel or mold steel Tungsten and molybdenum (good refractory qualities) used to die cast steel and cast iron ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

18 True Centrifugal Casting
©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

19 Cupola For Melting Cast Iron
"charge," consisting of iron, coke, flux, and possible alloying elements ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

20 Buoyancy in Sand Casting Operation
During pouring, buoyancy of the molten metal tends to displace the core Force tending to lift core = weight of displaced liquid less the weight of core itself Fb = Wm ‑ Wc Fb = buoyancy force Wm = weight of molten metal displaced Wc = weight of core ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

21 In-class Example An aluminum‑copper alloy casting is made in a sand mold using a sand core that weighs 20 kg. Determine the buoyancy force in Newtons tending to lift the core during pouring. Sand core density = 1.6 g/cm3 Al-Cu density = 2.81 g/cm3 ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

22 SME Video ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

23 In-class Assignment A sand core used to form the internal surfaces of a steel casting experiences a buoyancy force of N. What is the volume of the sand core in cm3? Steel density = 7.82 g/cm3 Sand core density = 1.6 g/cm3 ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

24 Extra Credit – hand in before test 1
Caplets are used to support a sand core inside a sand mold cavity. The design of the caplets and the manner in which they are placed in the mold cavity surface allows each caplet to sustain a force of 10 lbs. Several caplets are located beneath the core to support it before pouring; and several other caplets are placed above the core to resist the buoyancy force during pouring. If the volume of the core = 325 in3, and the metal poured is brass, determine the minimum number of caplets that should be placed (a) beneath the core, and (b) above the core. Brass density = lb/in3 ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

25 Manufacturing Economics
©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

26 Time Permitting Content
©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

27 Semicentrifugal & Centrifuge Casting
Semicentrifugal Casting Centrifuge Casting Density of part greater in outer sections Used for smaller parts Application: wheels and pulleys ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

28 Metal is melted without direct contact with burning fuel mixture
Crucible Furnaces Metal is melted without direct contact with burning fuel mixture lift‑out crucible stationary pot tilting-pot furnace ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

29 Electric‑Arc & Induction Furnaces
Heat generated by electric arc High power consumption for high melting capacity Primarily for melting steel Alternating current passing through a coil Develops magnetic field in metal Induced current rapidly heats and melts ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

30 Ladles & Additional Steps
Transfer of molten metal to mold Trimming Removing the core Surface cleaning Inspection Repair, if required Heat treatment crane ladle two‑man ladle ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

31 Casting Quality - General Defects
©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

32 Sand Casting Defects ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

33 Product Design Considerations
Original design Redesign Draft = 1 for sand casting Draft = 2 to 3 for permanent mold Allow 3 mm stock for machining Corners on the casting – source of stress concentration ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing 3/e

Download ppt "METAL CASTING PROCESSES"

Similar presentations

Chapter 11 METAL CASTING PROCESSES

Chapter 11 METAL CASTING PROCESSES
Metal Casting Processes Chapter 11- Part 1

Metal Casting Processes Chapter 11- Part 1
Manufacturing Processes

Manufacturing Processes
Ken YoussefiMechanical Engineering Dept., SJSU 1 Fundamentals of Casting Casting, one of the oldest manufacturing processes, dates back to 4000 B.C. when.

Ken YoussefiMechanical Engineering Dept., SJSU 1 Fundamentals of Casting Casting, one of the oldest manufacturing processes, dates back to 4000 B.C. when.
ME 330 Manufacturing Processes CASTING PROCESSES (cont.)

ME 330 Manufacturing Processes CASTING PROCESSES (cont.)
METAL CASTING PROCESSES

METAL CASTING PROCESSES
METAL CASTING PROCESSES

METAL CASTING PROCESSES
Metal Casting Processes Part 2

Metal Casting Processes Part 2
FUNDAMENTALS OF CASTING

FUNDAMENTALS OF CASTING
INTRODUNCTION Casting process is one of the earliest metal shaping techniques known to human being. Casting process consists of pouring molten metal into.

INTRODUNCTION Casting process is one of the earliest metal shaping techniques known to human being. Casting process consists of pouring molten metal into.
NC State University Department of Materials Science and Engineering1 MSE 440/540: Processing of Metallic Materials Instructors: Yuntian Zhu Office: 308.

NC State University Department of Materials Science and Engineering1 MSE 440/540: Processing of Metallic Materials Instructors: Yuntian Zhu Office: 308.
METAL CASTING PROCESSES

METAL CASTING PROCESSES
Casting. Die Metal is injected into the mould under high pressure of 10-210Mpa.Generally good surface finish and good dimensional accuracy. Typical Thin-walled:

Casting. Die Metal is injected into the mould under high pressure of Mpa.Generally good surface finish and good dimensional accuracy. Typical Thin-walled:
Permanent Mould Casting

Permanent Mould Casting
FUNDAMENTALS OF METAL CASTING

FUNDAMENTALS OF METAL CASTING
METAL CASTING PROCESSES

METAL CASTING PROCESSES
0 Casting since about 4000 BC… Ancient Greece; bronze statue casting circa 450BC Iron works in early Europe, e.g. cast iron cannons from England circa.

0 Casting since about 4000 BC… Ancient Greece; bronze statue casting circa 450BC Iron works in early Europe, e.g. cast iron cannons from England circa.
IE 337: Materials & Manufacturing Processes

IE 337: Materials & Manufacturing Processes
FUNDAMENTALS OF METAL CASTING

FUNDAMENTALS OF METAL CASTING
METAL CASTING PROCESSES 1.Foundry Practice 2.Casting Quality 3.Metals for Casting ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing.

METAL CASTING PROCESSES 1.Foundry Practice 2.Casting Quality 3.Metals for Casting ©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of Modern Manufacturing.