Manuel Maligas November 15, 2010 Subsea Bolting Failure With ASTM A320.

Slides:

Advertisements

Similar presentations

A local furniture making company has been finding it hard to sell expensive furniture due to the down turn in the economy. As a result they have been.

Advertisements

EXAMPLES OF WATER PUMP FAILURE MODES

IEC IEC Standard defines:

1. Introduction 2. Experimental 3. Results and discussion 4. Conclusions.

MINE CLEARING BLADE (MCB) DEADLINING COMPONENTS

SC6 Ballot 1974: Adopt-back of ISO 10423:2009 as API 6A 20 th ed. Task Group Report on Resolution of Ballot Comments Eric Wehner 30 June 2010.

Major Quality Failure Globalisation ‘The missing link’

Mill Rolls Introduction July  Company Profile  Facilities  Production  Products  Our Visions.

Metal Working. The term “Metal Working” generally refers to process of; joining, bending, casting, and cutting metal.

The Supreme Industries Ltd.,Gadegaon

One Eighty brings high level technology to real life problems that manufacturers and fabricators face. We provide engineering solutions. Solutions to.

BURN-IN, RELIABILITY TESTING, AND MANUFACTURING OF SEMICONDUCTORS

Presentation for SC17 Tuesday January 15, 2013

1 HYDROGEN EMBRITTLEMENT OF HIGH STRENGTH BOLTS American Galvanizers Association Tom Langill October 3rd, 2012.

Product Design and Qualification (Validation) Testing for HPHT Systems

Castings Mining Production Supply Li Ding. Topics: Introduction Background Products – Particular Piece Project I – Time Project Project II – Casting Quenching.

API Standard 6A718 Inclusion of Additional Alloy 718 Strength Classes

1 API SC6 Winter Meeting Other Materials Issues Tim Haeberle Chief Consulting Engineer – Materials and Processes GE Oil & Gas 4 February 2015.

T.M.F.T: Thermal Mechanical Fatigue Testing Wale Adewole Siyé Baker Heriberto Cortes Wesley Hawk Ashley McKnight.

BTEC First Engineering Unit 1: The Engineered World © Pearson Education Ltd Copying permitted for purchasing institution only. The first engineers.

Safety and quality issues – studs and nuts Presentation API 6A Winter meeting Feb

PPI for Water and Sewerage in Sweden 27th Voorburg Group meeting Warsaw, Poland October 4 th 2012.

Material failure analysis

Hydro Electric Generator FEA Analysis Ryan MacTarnaghan Mechanical Engineer Department of Water Resources.

1 Failures and fault classification Jørn Vatn NTNU

Vendor Management.  After selecting what to why? and how much to buy? There is a need to select from where to buy? i.e. the source of merchandise supply.

Managing Stress Corrosion Cracking Williams Gas Pipeline Transco – Ron Scrivner Northwest Pipeline – Dave Katz.

Annual report TC67/SC4/WG3 Wellhead and Xmass tree ISO10423vs API 6A WG Scope:standardisation of wellhead and xmass trees plus valves WG convenor :Ries.

API SC6 Winter Meeting New Business: API Standard 6A718 – Inclusion of Additional Alloy 718 Strength Classes - Inclusion of Additional Alloys Tim Haeberle.

VCA - Impact Resistance Testing Progam “10 easy steps to implement a low cost system”

The Point Pleasant Bridge Disaster The Collapse of “Silver Bridge”

Joining By: Skylar Baugher. Joining Examples ► Welding ► Brazing ► Soldering ► Diffusion Bonding ► Adhesive Bonding.

Welding Inspection and Metallurgy

Project specifications Division 1- general conditions Division 2- sitework Division 3- concrete Division 4- masonry Division 5- metals Division 6- carpentry.

Annual report TC67/SC4/WG3 Wellhead and Xmass tree ISO10423 and API 6A WG Scope:standardisation of wellhead and xmass trees plus valves WG convenor :Ries.

© 2007 Pearson Education, Inc. Publishing as Pearson Addison-Wesley 1 Mid-Level Design Patterns Categories.

13-2 Forgings Forging consists of plastically deforming, either by a squeezing pressure or sharp blows, a cast or sintered ingot, a wrought bar or billet,

PRODUCTION. Producing Products Production the multistep process of making parts and assembling them into products.

Status Report on Development of Cryo-ModuleTest Stand-1 (CMTS-1) for Fermi Lab Centre for Design & Manufacture Bhabha Atomic Research Centre Cryo-Module.

High-integrity fasteners for the world’s most demanding applications Quality | Strength | Honesty | Thoroughness | Responsiveness Thank you very much for.

SECAT PROVIDING ALUMINUM ANSWERS The scientists and engineers at Secat provide in-depth analysis using state-of-the-art metallurgical tools. Their advanced.

Contents Introduction Base Oil Market Trends Production Process

Aston International Manufacturer, supplier and Exporter of Brass Products /

Group 3 Steels: Eutectoid Composition Steels Steels with carbon contents just below the eutectoid to the eutectoid composition (0.6 – 0.8 C) are used.

Company profile and competences August Company identity 2.Facts & figures 3.Company vision 4.Casting cell overview, new investments, layout.

MGT 420 Week 4 DQ 2 What are some areas of a company adversely affected when switching suppliers? How would altering suppliers affect the different areas.

Root Cause Failure Analysis

National Academies of Sciences Workshop on Subsea Bolt Performance

High Strength Bolting vs. Subsea Service Conditions

Examples of Wheel Failures

Tim Mouzakis: FAA, Engine & Propeller Directorate

Materials Qualification for Bolting Applications

DEPARTMENT OF MECHANICAL AND MANUFACTURING ENGINEERING

Potential Risks, Limitations, And Failure Mechanisms Arising From Fastener Design, Manufacture, Material, And Coating Selection Prepared for the National.

14 Refrigerant Recovery, Recycling, and Recharging.

Properties of Steel.

Carry Over From API SC6 Winter Meeting API Standard 6A718 Inclusion of Additional Alloys Tim Haeberle 30 June 2011.

Carry Over From API SC6 Winter Meeting API Standard 6A718 Inclusion of Additional Alloy 718 Strength Classes Tim Haeberle 30 June 2011.

Presentation by Team 2.

UK Manufacturers & Suppliers of Gaskets, Rubber Mouldings, Inflatable Seals, Machined Components, Studbolts and more for many industries. STUDBOLTS & FASTENERS.

Committee on Standardization of Oilfield Equipment and Materials

May 26, 2014 EFFECT OF EXPLOSION CLADDING INDUCED HARDNESS ON SULFIDE STRESS CRACKING AND STRESS CORROSION CRACKING RESISTANCE OF INCONEL 625 Outline:

Alejandro F. Ameglio – Head Technical Services Tenaris Rods Division

التعامل مع ضغوطات العمل إعداد وتقديم إقبال المطيري

Products Hydrafit AS provides leading technology products for the on- and offshore market. Our products meet all relevant regulations and standards, both.

Structural safety – Studs and nuts

COMPANY NAME Business Continuity Plan Date Presented by.

C.2.10 Sample Questions.

C.2.8 Sample Questions.

C.2.8 Sample Questions.

Presentation transcript:

Manuel Maligas November 15, 2010 Subsea Bolting Failure With ASTM A320

Background Several failure occurred with major oil company operating in South American L7 Bolts were supplied by two Wellhead Manufacturing Companies Bolts were purchased from two fasteners companies Two raw material suppliers were used by the two fasteners companies Raw material supplied to fastener company was manufactured using continuously cast, in lieu of ingot cast Cause of failure was attributed to segregation Segregation resulted in a band of excessive hardness at interior of bolts Subsea bolts are connected to CP systems and are susceptible to stress cracking from high hardness

Current Practice ASTM A193 permits ingot or strand cast ASTM A962 permits ingots or continuously ASTMA320 has no requirements for melt practice but permits requirements of ASTM A320 ??962?? to prevail

Microstructure of Failed Bolts

Segregation Failure Mechanisms Sea Water + CP + = + = H2S Hard Ban

Discussion Applicable to 6A: USV valves and exposed bolting Use of the continuous cast process is increasing Since no requirement is included in ASTM A320, suggest that ingot cast be specified Standard macro hardness is not sufficient for detection Standard sample size is not sufficient for detection