LDPE PRODUCTS – TEHNICAL INFORMATION

1 LDPE GRADES

2 LDPE – B20/0.3 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min0,3ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A –50°C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 1) PRODUCT DESCRIPTION: low density polyethylene, ethylene homopolymer without stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, for blown film, extra heavy-duty bags.

3 LDPE – B22/0.25 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min0,25ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 1) PRODUCT DESCRIPTION: low density polyethylene, homopolymer with antioxidant stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, shrink film.

4 LDPE – 21/0.5 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min0,5ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 1) PRODUCT DESCRIPTION: low density polyethylene, ethylene homopolymer with slip and antiblocking agent stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, film for liquid packaging, co-extrusion film.

5 LDPE – B22/0.7 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min0,7ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 HAZE%13ASTM D1003 1) PRODUCT DESCRIPTION: low density polyethylene, homopolymer with antioxidant stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APLICATIONS: extrusion, agriculture film, and protection film.

6 LDPE – B22/1 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min1ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 HAZE%13ASTM D1003 1) PRODUCT DESCRIPTION: low density polyethylene, homopolymer with antioxidant stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APLICATIONS: extrusion, agriculture film, and protection film.

7 LDPE – B21/2 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min2ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 HAZE%8ASTM D1003 GLOSS, 45 0 UL60ASTM D2547 1) PRODUCT DESCRIPTION: low density polyethylene, ethylene homopolymer with slip and antiblocking agent stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, film for fine packaging with a good transparency.

8 LDPE – B20/2 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min2ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 HAZE%8ASTM D1003 GLOSS, 45 0 UL60ASTM D2547 1) PRODUCT DESCRIPTION: low density polyethylene, ethylene homopolymer without stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, film for fine packaging with a good transparency.

9 LDPE – B20/3 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min3ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 HAZE%7ASTM D1003 GLOSS, 45 0 UL60ASTM D2547 1) PRODUCT DESCRIPTION: low density polyethylene, ethylene homopolymer without stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, film for fine packaging with a very good transparency and gloss.

10 LDPE – B21/3 PROPERTIESMUVALUETEST METHOD APPEARANCEUniform color granules, without extraneous matter. Are allowed max.0, 01 %m/m contaminants (oxidizes and other defects). VISUAL MELT FLOW INDEX (190 o C / 2.16 kg) g/10min3ASTM D1238 DENSITY (23 o C)g/cm 3 0,92ASTM D792 VICAT SOFTENING TEMPERATURE (A -50 o C/h-10N) 0C0C100ISO 306/A TENSILE STRENGHT AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction MPa ISO 527/3 ELONGATION AT BREAK (23 o C, v=500mm/min) Machine direction Cross direction % ISO 527/3 HAZE%7ASTM D1003 GLOSS, 45 0 UL60ASTM D2547 1) PRODUCT DESCRIPTION: low density polyethylene, ethylene homopolymer with slip and antiblocking agent stabilization. Ethylene monomer is the only monomer used for producing the macromolecular product. For producing the above-mentioned grade there are not used plasticizers or colored master batches. The product has natural color. 2) APPLICATIONS: extrusion, film for extra fine packaging with a very good transparency and gloss

11 Thank You !