Best Available Techniques in the Ferrous Metals Processing Industry EUROPEAN COMMISSION Best Available Techniques in the Ferrous Metals Processing Industry Gestión Ambiental Curso 2007-08 Grupo 3: Abad González, Soraya Prada Uña, Raquel Rodríguez Gutiérrez , Cristina Villacorta Asensio, Milagros

A.1 Wire A.1 General Information Hot and Cold Formed Products covered by this BREF: A.1 General Information We´re going to talk about WIRE Asignatura: Gestión Ambiental - Curso 2007-2008

A.2 Wire A.2 Processes and Techn. A.2.1 Wire Drawing Process A typical wire drawing process line comprises the following steps: Pre-treatment of the wire rod (mechanical descaling, pickling). Dry or wet drawing (usually several drafts with decreasing die sizes). Heat treatment (continuous-/discontinuos annealing, patenting, oil hardening). Finishing. Wire drawing is a process in which wire rods/wires are reduced in size by drawing them through cone-shaped openings of a smaller cross section, so called dies. The input usually is wire rod of diameters raging from 5.5 to 16.0 mm obtained from hot rolling mills in form of coils. A.2 Processes and Techn. Asignatura: Gestión Ambiental - Curso 2007-2008

A.2 Wire A.2 Processes and Techn. A.2.1.1 Wire Rod Preparation Air-cooling after rolling produces an iron oxide-layer (scale) on the wire rod surface. This layer is very hard, brittle and not deformable and must therefore be removed before any further processing can take place. Two techniques for descaling wire rods are applied: A.2.1.2 Drawing Dry Drawing of Wire Dry drawing is typically used to draw wire rod (> 5.5 mm) to a product diameter of 1 - 2 mm . Wet Drawing of Wire Wet drawing is typically used to draw wire with an intermediate product diameter of 1 - 2 mm to final diameter. Mechanical descaling Chemical pickling A.2 Processes and Techn. Asignatura: Gestión Ambiental - Curso 2007-2008

A.2 Wire A.2 Processes and Techn. A.2.1.3 Heat Treatment of Wire Heat treatment of wire has different goals. Different types of heat treatment are available depending on the type of steel and the final use. Heat treatment also thermally removes soap and lubricant residues. A considerable percentage of the output of the wire industry does not need any heat-treatment. Annealing is one of the different methods to re-obtain a suited crystal shape. Batch Annealing of Low Carbon Steel Wire. Continuous (In-Line) Annealing of Low Carbon Steel Wire. Continuous (In-Line) Annealing of Stainless Steel Wire. A.2 Processes and Techn. Asignatura: Gestión Ambiental - Curso 2007-2008

A.2 Wire A.2 Processes and Techn. Patenting Patenting is a heat-treatment method typically used for high-carbon and alloyed steel products to create a special crystal structure, which allows easy further deformation. Patenting is done by heating the wire to 850 - 1000 °C, then cooling fast to 450 - 600 °C. Patenting is usually done continuously. Stress-relieving The goal of stress-relieving is to remove internal stresses in the wire caused by a previous processing steps, without changing the shape and structure of the steel crystal. Stress-relieving can be done at various temperatures (200 - 500 °C), dependent on the desired characteristics of the final product. A.2 Processes and Techn. Asignatura: Gestión Ambiental - Curso 2007-2008

A.2 Wire A.2 Processes and Techn. A.2.1.4 In- line Pickling In-line pickling is a typical operation after heat-treatment and/or before hot-dip coating of wire. It is used to clean the wire and to remove metal oxides. The wire is passed continuously through one or more acid baths. The pickling takes place in a very short time (a few seconds). After pickling the wire is rinsed in water. A.2 Processes and Techn. Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.1 Mass Stream Overview Input/Output balance for a wire mill. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.2 Wire Rod Preparation A.3.2.1 Mechanical Descaling of Wire Rod Mechanical descaling brings about solid waste: Scale, mainly consisting of iron oxide (FeO and Fe3O4) Traces of other metal oxides A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.2.2 Chemical Descaling/Pickling of Wire Rod In chemical descaling liquid waste is generated in form of spent HCl or H2SO4 acid. Aerosols can from mechanically when the wire rod is allowed to drip off. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.2.3 Application of Soap Carrier Consumption and emissions associated with the application of soap carrier vary in dependence of the type of soap carrier, thickness applied and the wire rod diameter. No quantitative data is available at the moment. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.3 Drawing of Wire A.3.3.1 Dry Drawing Dry drawing activities leave spent lubricant: mainly consisting of the drawing soap itself contaminated by degradation products. Also soap dust arises, which can be controlled by proper encapsulation and filtering of the extracted air. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.3.2 Wet Drawing Wet drawing is done in a watery emulsion of soap or oil is gradually contaminated by dragin of various products from previous process steps. The result is that the wet drawing lubricant needs to be replaced from time to time: The replacement frequency can be lowered by continuous removal of some of the contaminants by decantation or filtration. Other waste streams are broken dies and cooling tower blowdown. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.4 Heat Treatment of Wire A.3.4.1 Batch Annealing/Bell and Pot Furnaces Emissions from batch annealing furnaces comprises: - The combustion products from the firing - A small flow of the protective atmosphere (purge) containing decomposition products of the lubricant A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.4.2 Continuous Annealing/Molten Lead Bath This process leads to solid wastes in the form of lead oxides and lead contaminated bath cover material. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.4.3 Patenting Wastes and emissions are: - Air emissions arise from the furnace. Fresh air is mixed with the hot exhaust gas of the oven in order to convert the CO to CO2, prior to emission into the atmosphere. NOx and SO2 are negligible in this stream: reducing atmosphere/fuel is free of sulphur - Solid waste is generated by the lead bath as lead oxides and spent bath cover material - Waste water is formed in the quench bath A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.4.4 Oil Hardening & Tempering Waste and emissions are dependent on: - The method of heating - The quench medium - The reheating method A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.4.5 Annealing of Stainless Steel Wire A quantitative mass balance cannot be given. A.3.4.6 Stress Relieving The most important application is stress relieving of PC-strand: reinforcement wire that will be used in prestressed concrete. A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.3 Wire Plant A.3 Emission Levels A.3.5 Noise Issues in a Wire Plant The main sources of noise in wire processes are: - Rotating equipment - Air-wipes or air-brushes which clean the wire using compressed air can have a high frequency noise - Pay-off units of wire rod have a particular repetitive noise - Burners of ovens A.3 Emission Levels Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques Reference Document on Best Available Techniques in the Ferrous Metals Processing Industy A.4 Wire Mill A.4.1 Storage and Handling of Raw Materials and Auxiliares Description: All storage tanks for both fresh and spent acid must be equipped with a sealed secondary containment. This secondary containment must be protected with an acid-resistant coating. The loading and unloading area for the acids any potential leak is directly discharged to the waste water treatment plant. A.4.2 Mechanical Descaling A.4.2.1 External Recycling of Scale The scale from mechanical descaling of wire consists mainly of metal oxides ( which is oild and water free). This scale can be recycling to recovery the iron content. Recycling is done or not depends to the interests of the industry. Main achieved environmental benefits: Reduction to waste. A.4 Techniques Utilice esta plantilla para crear páginas Web de intranet para un grupo de trabajo o proyecto. Puede modificar el contenido de muestra para incluir la información que desee e incluso puede cambiar la estructura del sitio Web agregando y quitando diapositivas. Los controles de desplazamiento están en el patrón de diapositivas. Para cambiarlos, en el menú Ver, seleccione Patrón y, a continuación, elija Patrón de diapositivas. Para agregar o quitar hipervínculos en el texto o los objetos, o para cambiar los hipervínculos existentes, seleccione el texto o el objeto y elija Hipervínculo en el menú Insertar. Cuando termine de personalizar la presentación, elimine estas notas para ahorrar espacio en los archivos HTML finales. Para obtener más información, consulte en el Asistente para Ayuda los siguientes temas: Patrón de diapositivas Hipervínculos Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.3. Chemical Descaling/ Pickling of Wire Rod A.4.3.1 Optimum Range of Operation for HCl Pickling Baths Main achieved environmental benefits: Reduction of acid emissions to air. A.4.3.2 Pickling Tank Fume Control Description: Vapour and aerosols comming off tanks can be controlled by: Reduction of acid vapours and aerosols emissions Reduction of fugitive emissions. Improvement of working environment, protection of installation and equipment A.4.3.3 Treatment of Extracted Air from Pickling Tank Fume Control For reduction of acid vapour, droplets or aerosols emission can be used Demister (for H2SO4) or scrubber (for HCl) Reduction of acid vapour, droplets and aerosols emissions. Hoods Lateral extractions A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.3.4 Cascade Pickling Main achieved environmental benefits: Reduced consumption of fresh acid Reduced spent acid (waste) A.4.3.5 Minimizing Carry-out from Pickling Reduced carry-out of acid, reduced consumption of fresh acid Reduced pickling loss. A.4.3.6 Separation and Reuse of Free Acid Fraction A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.3.7 Regeneration of Spent Acid Main achieved environmental benefits: Reduction of acidic waste A.4.3.8 Reuse of Spent Acid as Secondary Raw material A.4.3.9 Minimize Rinsing Water Consumption by Cascade Rinsing Reduction of water consumption A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.4 Shot Blast Descaling: Separation of Scale and Blast media Description: The shot blast system causes the scale to break and fall off the base metal The blast cabinet descaling operation The reclaim system retrieve the used shot and dust from the descaling operation The recycling system separating the shot particles from the contaminants and dust the cleaned shot particles are returned to a storage system Main achieved environmental benefits: Scale is collected separately and can be reused Consumption of shot-blasting media is reduced A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.5 Dry Drawing A.4.5.1 Control of Air Emissions /Treatment of Extracted Air Description: A hood or cover is installed above of the parts (of machine) in contact with wire The air within the cover is extracted The extracted air can be treated by a filter Main achieved environmental benefits: Reduction of emissions to air Improvement of working enviroment limit the spread of lubricant-dust over the area around the drawing machine A.4.5.2 Closed Loop for Cooling Water The drawing operation heats both wire and drawing die both the dies and the wire are water cooled. To reuse the cooling water Wet cooling tower Reduction water consumption A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.6 Wet Drawing A.4.6.1 Closing loop for cooling water Description: The drawing operation heats both wire and drawing die through friction of the wire. This heat is taken up by the lubricant Main achieved environmental benefits: Reduced water consumption. A.4.6.2 Cleaning of drawing lubricant/coolant Wire drawing lubricants, water-miscible oil emulsions or straight oils, accumulate metal fines during operation Reduccion of waste drawing lubricant A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.7 Batch Annealing of Wire A.4.6.3 Treatment and Disposal of Waste Drawing Lubricant: Soap Emulsions Description: In case the quantities are small compared to other waste waters of the plant, the spent lubricant is mixed with otherwaste waters. If the quantities are comparably big, the spent lubricants are treated separately by coagulation and precipitation, coagulation and flotation, membrane filtration, evaporation or other suited methods. Main achieved environmental benefits: Reduced emissions to water A.4.7 Batch Annealing of Wire A.4.7.1 Burn Purge of Protective Gas In order to keep an over-pressure in the "pots" or "bells", a fraction of the protective gas is continuously purged. Reduced emissions to air A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4.8 Continuous (in-line) Annealing of Low Carbon Wire A.4.8.1 Lead-bath: Good Housekeeping Description: Maintain a protective layer or cover on the lead-bath Prevent formation of dust while removing impurities from the lead-bath Minimize drag-out of lead with the wire by using an anthracite gravel wipe or similar immediately after the lead bath Apply a method that minimizes / eliminates the spread of lead dust that is possibly dragged out with the wire. Main achieved environmental benefits: Reduce emissions from lead bath A.4.8.2 Recycling of Pb- containing residues Some Pb-containing residues originate from the Pb-bath. These residues should be stored separately and protected from rain and wind. The wire industry depends on subcontractors for the final disposal or recycling of these residues. Reduced waste disposal A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.9 Patenting A.4.8.3 Operation of Quench Bath and treatment of waste water from quench baths in-line annealing Description: As the water quality requirements for this bath are generally low, it is advised to use recuperated water for this purpose or to operate the quench bath in closed loop. Main achieved environmental benefits: Reduced emissions to water A.4.9 Patenting A.4.9.1 Optimised Operation of the Oven A slightly substochiometric mixture is used in the burners. In this way, all O2 is excluded from the oven atmosphere, in order to minimize the formation of iron oxides at the wire surface Excess CO must be converted to CO2 by adding air in a controlled way to the hot exhaust of the oven. Reduced consumption in following process steps Reduced CO-content A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.4 Wire Mill A.4 Techniques A.4.10 Oil Hardening and Tempering Description: Evacuation of the oil mist and removal from the extracted air Main achieved environmental benefits: Reduction of fugitive air emissions, especially oil emissions. A.4.11 Heat Treatment of Wire (Different Processes) A.4.11.1 Inductive Heating of wire The wire to be heated is guided through a coil; in this coil a magnetic field is generated. The applicability of inductive heating is highly dependent on wire material, wire diameter and required temperature increase: Air emissions from combustion are avoided in the plant A.4 Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

A.5 Wire Plant For batch pickling, the following techniques are considered to be BAT: HCl pickling: close monitoring of bath parameters: temperature and concentration. • In the case of high vapour emission: installation of lateral extraction and possibly treating of the extraction air for both new and existing installations. To reduce acid consumption, amounts of acidic wastes and waste water, the following techniques are considered to be BAT: Cascade Pickling or reclamation of free acid fraction and reuse in pickling plant. • External regeneration of spent acid. • Recycling of spent acid as secondary raw material. Non-acid descaling if quality requirements allow. • Countercurrent cascade rinsing For wet drawing lubricants, the following measures are considered to be BAT: • Cleaning and reuse of drawing lubricant. • Treatment of spent lubricant to reduce oil content in the discharge and/or to reduce waste volume. • Treatment of discharge water fraction. A.5 BAT Asignatura: Gestión Ambiental - Curso 2007-2008

A.5 Wire Plant The best available techniques to reduce cooling water consumption are closed cooling-water loops for dry and wet drawing. Burning of the protective gas purge is considered to be BAT for all batch annealing furnaces, continuous annealing furnaces for stainless steel and furnaces used in oil hardening and tempering For continuous annealing of low carbon wire and patenting, the following measures are considered to be BAT: • Recycling of Pb-containing wastes in non-ferrous metals industry • Closed loop operation of quench bath. A.5 BAT Asignatura: Gestión Ambiental - Curso 2007-2008

A.6 Wire Plant A.6 Emerging Techniques Acid regeneration process such as electrodialysis / bipolar membrane technology are under development or being tested. This technology which converts all acid again to free acid and metals to hydroxides is much too young / not proven / too expensive From analogy with more traditional membrane processes, a short membrane life is expected. A.6 Emerging Techniques Asignatura: Gestión Ambiental - Curso 2007-2008

Best Available Techniques in the Ferrous Metals Processing Industry EUROPEAN COMMISSION Best Available Techniques in the Ferrous Metals Processing Industry Gestión Ambiental Curso 2007-08 Grupo 3: Abad González, Soraya Prada Uña, Raquel Rodríguez Gutiérrez , Cristina Villacorta Asensio, Milagros