LDC borstplätering www.ldc-brushplating.com2 LDC Portable Electroplating 1.Cold process: used at room temperature, no stress or adjustments because of.

Similar presentations


Presentation on theme: "LDC borstplätering www.ldc-brushplating.com2 LDC Portable Electroplating 1.Cold process: used at room temperature, no stress or adjustments because of."— Presentation transcript:

1

2 LDC borstplätering LDC Portable Electroplating 1.Cold process: used at room temperature, no stress or adjustments because of termal distorsion. 2.To tolerance: normally no machining required 3.Quick metal build-up: 0,05 mm in min. 4.Plating: on all conductive materials, cast iron, stainless, mild steel, copper, chrome etc 5.Dense deposits: no or very little porosity in most coatings 6.Many differens metals: nickel, gold, silver, copper, cobolt, zinc and alloys. 7.Excellent bonding: molecular bonding results in very god adhesion, all coatings can be machined, ground or polished. 8.Mobile equipment: the repair can be done on site

3 3 On site repair of the crankshaft in a conversion press. LDC borstplätering Tele:

4 4 LDC borstplätering Tele: Damaged /worn flywheel bearing areas on the crankshaft in a conversion press.

5 5 LDC borstplätering Tele: Prepare and masking off surrounding areas.

6 6 Plating procedure going on. LDC borstplätering Tele:

7 7 Damaged bearing journal plated to size. LDC borstplätering Tele:

8 8 LDC borstplätering Tele: Crankshaft is finished and the original tolerances and measurements are obtained. Ready to assemble the flywheel.

9 9 Repair on site. Lower bed die in a conversion press with local wear damages LDC borstplätering Tele:

10 10 Plated/repaired damage on the lower bed die. LDC-2904 copper hi-speed HB250 were used to fill the damage up. Top coated with LDC-2807 Nickel acid for wear and corrosion protection. LDC borstplätering Tele:

11 11 Repair on site. Lower bed die in a conversion press with local wear damages LDC borstplätering Tele:

12 12 Damaged area in the lower bed die. LDC borstplätering Tele:

13 13 One worn out slide. There are damages from the pistons and micro vibrations. And causes oil leaking. LDC borstplätering Tele:

14 14 Damaged area inside the slide LDC borstplätering Tele:

15 15 The damages is being plated with a hard copper of 250 Brinell and grinded to original tolerances. LDC borstplätering Tele:

16 16 Area has now a new top coating with a nickel with a hardness of 400 brinell and also gives a excellent protection from new damages. LDC borstplätering Tele:

17 17 Plating is now finished and the slide is ready for assembly. LDC borstplätering Tele:

18 18 Oil leakage from scratched and damaged main pistons brush plated on site. LDC borstplätering Tele: