1. Welcome to QMI QMI Paint Sealant Presentation

2. Teflon ® / PTFE Dynamic Utilized since 1938 –Auto racing –Aircraft –Space travel Numerous applications, including Paint Sealant –Heavy industry

3. PTFE Chemical Formula (CF 2 CF 2 ) n C = Carbon –backbone of universe F 2 = Fluorine –low surface energy –chemically inert

4. PTFE Chemical Bonds 1.Carbon to Carbon forms backbone 2.Carbon to Fluorine forms shield Powerful binding forces

5. PTFE Fluorine Shield Carbon backbone surrounded by sheath of large fluorine atoms Low surface energy –Low coefficient of friction –Non-sticking Powerfully bonded –Fracture resistance –High thermal stability Large fluorine atoms –Other atoms cannot penetrate –Chemically inert

6. PTFE Moisture / Humidity Hydrophobic –Does not combine with water –Does not dissolve in water Resistant to hydrolysis –Does not decompose, react with water Barrier to water permeation –Stable after year-long water immersion

7. PTFE Light & Age Stability Transparent to ultraviolet light Resistant to: –Oxidation –Surface fouling –Discoloration –Embrittlement Proven 20-year Florida test

8. PTFE Long Service Life Retains properties after aging Withstands exposure to: –High temperature 780°F / 415°C –Solvents –Oils –Oxidizing agents –Ultraviolet light –Other environmental agents

9. Combined Ingredient Benefits Ultimate shine & protection Hard, mirror-like finish Sun shield protects paint against fading Never turns gray or yellow when exposed to sunlight Seals against oxidation, corrosives, salts, dirt and insects Dirt and grime wash off easily Unsurpassed durability

10. Method of Application Easy to apply –By hand –By orbital buffer Removes road film and detergent build-up –Often eliminates need to use rubbing compounds

11. Applications –Non-abrasive, safe for clear-coat finishes Fiberglass and formica –Counter tops, sinks, bath tubs, showers, etc. –Automobiles, trucks, marine, aircraft, etc. Approved for enamel, lacquer, metal flake and metallic painted surfaces

12. Q-LAB Test - QMI & CPC Q-Lab Weathering Research Service –Accelerated weather gloss test 10 painted panels, 75 mm x 152 mm –5 QMI panels, 5 CPC panels –Each panel polished and buffed –Test cycle 8 hours UV light 4 hours condensation (moisture) –Gloss reading every 100 hours 500 hours represent approximately 6 months

13. QMI / CPC Test Results SpecimenOriginalPresentChangeCombined Change QMI 100 hrs. QMI 200 hrs. QMI 300 hrs. QMI 400 hrs. QMI 500 hrs. 83 82 84 82 85 82 1 0 -3 2 Total gloss change on 5 plates: - 1 point (gloss increase) Average gloss change per plate: -0.5 point (gloss increase) CPC 100 hrs. CPC 200 hrs. CPC 300 hrs. CPC 400 hrs. CPC 500 hrs. 88 89 87 86 88 85 86 84 82 3332633326 Total gloss change on 5 plates: 17 points (gloss decrease) Average gloss change per plate: 3.4 points (gloss decrease) Q-LAB Report No. 1 — 100 Hours

14. QMI / CPC Test Results SpecimenOriginalPresentChangeCombined Change QMI 200 hrs. QMI 300 hrs. QMI 400 hrs. QMI 500 hrs. 83 82 84 80 82 84 81 3 0 -2 3 Total gloss change on 4 plates: 4 points (gloss decrease) Average gloss change per plate: 1 point (gloss decrease) CPC 200 hrs. CPC 300 hrs. CPC 400 hrs. CPC 500 hrs. 89 87 86 88 85 84 83 82 43364336 Total gloss change on 4 plates: 16 points (gloss decrease) Average gloss change per plate: 4 points (gloss decrease) Q-LAB Report No. 2 — 200 Hours

15. QMI / CPC Test Results SpecimenOriginalPresentChangeCombined Change QMI 300 hrs. QMI 400 hrs. QMI 500 hrs. 82 84 81 83 81 1 3 Total gloss change on 3 plates: 3 points (gloss decrease) Average gloss change per plate: 1 point (gloss decrease) CPC 300 hrs. CPC 400 hrs. CPC 500 hrs. 87 86 88 83 343343 Total gloss change on 3 plates: 12 points (gloss decrease) Average gloss change per plate: 4 points (gloss decrease) Q-LAB Report No. 3 — 300 Hours

16. QMI / CPC Test Results SpecimenOriginalPresentChangeCombined Change QMI 400 hrs. QMI 500 hrs. 82 84 83 82 2 Total gloss change on 2 plates: 1 point (gloss decrease) Average gloss change per plate: 0.5 point (gloss decrease) CPC 400 hrs. CPC 500 hrs. 86 88 81 82 5656 Total gloss change on 2 plates: 11 points (gloss decrease) Average gloss change per plate: 5.5 points (gloss decrease) Q-LAB Report No. 4 — 400 Hours

17. QMI / CPC Test Results SpecimenOriginalPresentChangeCombined Change QMI 500 hrs.84822Total gloss change on 1 plate: 2 points (gloss decrease) CPC 500 hrs.88835Total gloss change on 1 plate: 5 points (gloss decrease) Q-LAB Report No. 5 — 500 Hours

18. Average Gloss Decrease

19. Total Gloss Decrease - 500 Hours

20. QMI Paint Sealant The perfect solution for today’s polishing needs Thank you!

21. It’s time...