1. Chapter 15 Metal Extrusion and Drawing Processes and Equipment

2. EXTRUSION a cylindrical billet is forced through a die DRAWING the cross section of a solid rod , wire or tube is reduced or changed in shape by pulling it through a die

3. FIGURE 15.1 Schematic illustration of the direct-extrusion process.

4. FIGURE Extrusions and examples of products made by sectioning off extrusions. Source: (d) Courtesy of Plymouth Extruded Shapes. (For extruding plastics, see Section 19.2.)

5. FIGURE 15.3 Types of extrusion: (a) indirect; (b) hydrostatic; and (c) lateral.

6. PROCESS VARIABLES reduction in cross sectional area die angle extrusion speed billet temperature lubrication

7. FIGURE Process variables in direct extrusion; the die angle, reduction in cross-section, extrusion speed, billet temperature, and lubrication all affect the extrusion pressure.

8. TABLE Typical Extrusion Temperature Ranges for Various Metals and Alloys. (See also TABLE 14.3.)

9. FIGURE Typical extrusion die shapes: (a) die for nonferrous metals; (b) die for ferrous metals; and (c) die for a T-shaped extrusion made of hot-work die steel and used with molten glass as a lubricant. Source: (c) Courtesy of LTV Steel Company.

10. FIGURE Extrusion of a seamless tube (a) using an internal mandrel that moves independently of the ram: an alternative arrangement has the mandrel integral with the ram and (b) using a spider die (see Fig. 15.9) to produce seamless tubing.

11. FIGURE 15.11a Two examples of cold extrusion; the arrows indicate the direction of metal flow during extrusion.

12. FIGURE 15.11b Two examples of cold extrusion; the arrows indicate the direction of metal flow during extrusion.

13. IMPACT EXTRUSION

14. FIGURE Schematic illustration of the impact-extrusion process; the extruded parts are stripped by using a stripper plate.

15. DESIGN CONSIDERATIONS 1. symmetry of cross section 2
DESIGN CONSIDERATIONS 1. symmetry of cross section 2. Avoid hollow cross sections 3. Avoid a critical dimension in a cross-section 4. Avoid wide thin sections

16. FIGURE Examples of poor and good design practices for extrusion; note the importance of eliminating sharp corners and keeping section thicknesses uniform.

17. FIGURE General view of a 9-MN (1000-ton) hydraulic-extrusion press. Source: Courtesy of Jones & Laughlin Steel Corporation.

18. DRAWING the major processing variables are the same as extrusion: die angle, reduction in area, drawing speed and friction along the die-work piece interface extrusion: material is pushed through the die drawing: material is pulled through the die

19. FIGURE Process variables in wire drawing; the die angle, reduction in cross-sectional area per pass, speed of drawing, temperature, and lubrication condition all affect the drawing force, F.

20. FIGURE Examples of tube-drawing operations, with and without an internal mandrel; note that a variety of diameters and wall thicknesses can be produced from the same initial tube stock (which has been made by other processes).

21. FIGURE Cold drawing of an extruded channel on a draw bench to reduce its cross-section; individual lengths of straight rods or of cross-sections are drawn by this method.

22. FIGURE An illustration of multistage wire drawing typically used to produce copper wire for electrical wiring. Shown is a five bull block configuration; wire drawing machines can incorporate 15 or more of these drums, depending on the material and wire size. Source: After H. Auerswald.