1. Chapter 11 Properties and Processing of Metal Powders, Ceramics, Glasses, Composites and Superconductors

2. Powder-Metallurgy Processes
FIGURE (a) Examples of typical parts made by powder-metallurgy processes. (b) Upper trip lever for a commercial irrigation sprinkler, made by P/M. this part is made of unleaded brass alloy; it replaces a die-cast part, with a 60% savings. Source: Reproduced with permission from Success Stories on P/M Parts, Princeton, NJ: Metal Powder Industries Federation, 1998.

3. Particle Shapes
FIGURE Particle shapes in metal powders and the processes by which they are produced. Iron powders are produced by many of these processes.

4. Methods of metal-powder production by atomization
FIGURE Methods of metal-powder production by atomization: (a) melt atomization and (b) atomization with a rotating consumable electrode.

5. Weight/Particle Size Distributions
FIGURE (a) A plot of the weight of particles as a function of particle size. The most populous size is termed the mode. In this case, it is between 75µm and 90µm. (b) Cumulative particle-size distribution as a function of weight. Source: Reprinted with permission from Randall M. German, Powder Metallurgy Science, Princeton, NJ: Metal Powder Industries Federation, 1984.

6. Compaction of P/M Parts
FIGURE (a) Compaction of metal powder to form a bushing. the pressed-powder part is called green compact. (b) Typical tool and die set for compacting a spur gear. Source: Reprinted with the permission of the Metal Powder Industries Federation.

7. Density/Compacting Pressure
FIGURE (a) Density of copper-and iron-powder compacts as a function of compacting pressure. Density greatly influences the mechanical and physical properties of P/M parts. Source: F. V. Lenel, Powder Metallurgy: Principles and Applications, Princeton, NJ: Metal Powder Industries Federation, Reprinted by permission of Metal Powder Industries Federation, Princeton, NJ. (b) Effect of density on tensile strength, elongation, and electrical conductivity of copper powder. IACS means International Annealed Copper Standard for electrical Conductivity.

8. Density Variation
FIGURE Density variation in compacting metal powders in different dies: (a) and (c) single-action press; (b) and (d) double-action press. Note in (d) the greater uniformity of density in pressing with two punches with separate movements as compared with (c). Generally, uniformity of density is preferred, although there are situations in which density variation, and hence variation of properties, within a apart may be desirable. (e) Pressure contours in compacted copper powder in a single-action press. Source: P. Duwez and L. Zwell.

9. Stresses in Compaction
FIGURE Coordinate system and stresses acting on an element in compaction of powders. The pressure is assumed to be uniform across the cross-section. (See also Fig. 6.4.)

10. Compacting Pressures
TABLE Compacting pressures for various metal powders.

11. Sintering Temperatures
TABLE Sintering temperatures and times for various metal powders.

12. Sintering Metal Powders
FIGURE Schematic illustration of two mechanisms for sintering metal powders: (a) solid-state material transport; and (b) liquid-phase material transport. R = particle radius, r = neck radius, and p = neck profile radius.

13. Elongation/Sintering Time and Temperature
FIGURE Effect of sintering temperature and time on elongation and dimensional change during sintering of type-316L stainless steel. Source: ASM International.

14. Mechanical Properties of P/M Materials
TABLE Typical mechanical properties of selected P/M materials.

15. Mechanical Property Comparison
TABLE Mechanical property comparisons for Ti-6Al-4V titanium alloy.

16. Main Bearing Caps
FIGURE Powder-metal main bearing caps for 3.8- and 3.1-liter GM engines. Source: Courtesy of Zenith Sintered Products, Inc., Milwaukee, WI.