1. Chapter 11: Applications and Processing of Metal Alloys
ISSUES TO ADDRESS...
• How are metal alloys classified and what are their common applications?
• What are some of the common fabrication techniques
for metals?
• What heat treatment procedures are used to improve the
mechanical properties of both ferrous and nonferrous alloys?

2. Classification of Metal Alloys
Adapted from Fig. 11.1, Callister & Rethwisch 9e.
Ferrous
Nonferrous
_______
_________
Steels
__________
___________
Cast Irons
<1.4wt%C
3-4.5
wt%C
microstructure: ferrite,
graphite/cementite Fe 3 C
cementite
1600
1400
1200
1000
800
600
400 1 2 4 5 6
6.7 L γ
austenite
γ + L
γ + Fe3C α
ferrite
α + Fe3C +
L+ Fe3C δ
(Fe)
Co , wt% C
Eutectic:
Eutectoid:
0.76
4.30
727ºC
1148ºC
T(ºC)
Fig. 9.24, Callister & Rethwisch 9e.
[Adapted from Binary Alloy Phase Diagrams, 2nd edition, Vol. 1, T. B. Massalski (Editor-in-Chief), Reprinted by permission of ASM International, Materials Park, OH.]

3. Steels Low Alloy High Alloy low carbon <0.25 wt% C Med carbon
high carbon
wt% C
plain
HSLA
heat
treatable
tool
stainless
Name
Additions
none
Cr,V
Ni, Mo
Cr, Ni Mo
Cr, V,
Mo, W
Cr, Ni, Mo
Example
1010
4310
1040 43 40
1095
4190
304, 409
Hardenability + ++
+++
varies TS - + ++
varies EL + + - - -- ++
Uses
auto
bridges
crank
pistons
wear
drills
high T
struc.
towers
shafts
gears
applic.
saws
applic.
sheet
press.
bolts
wear
dies
turbines
vessels
hammers
applic.
furnaces
increasing strength, cost, decreasing ductility
blades
Very corros.
resistant
Based on data provided in Tables 11.1(b), 13.2(b), 11.3, and 11.4, Callister & Rethwisch 9e.

4. Refinement of Steel from Ore
Iron Ore
_____
______________
3CO +
Fe2O3
2Fe
+3CO2 C + O2
CO2
2CO
CaCO3
CaO+CO2
CaO + SiO2 + Al2O3
slag
purification
reduction of iron ore to metal
heat generation
Molten iron
BLAST FURNACE
air
layers of _____
and _________
gas
refractory
vessel

5. Ferrous Alloys Iron-based alloys • Steels • Cast Irons
Nomenclature for steels (AISI/SAE)
10xx ___________________
11xx Plain Carbon Steels (resulfurized for machinability)
15xx Mn ( %)
40xx Mo (0.20 ~ 0.30%)
43xx Ni ( %), Cr ( %), Mo ( %)
44xx Mo (0.5%)
where xx is wt% C x 100
example: steel – plain carbon steel with 0.60 wt% C
_______________________ >11% Cr
• Steels
• Cast Irons

6. Cast Irons Ferrous alloys with > ______________
more _________________________
Low melting – relatively easy to cast
Generally brittle
Cementite decomposes to ______ + _______
Fe3C  3 Fe (α) + C (____________)
generally a slow process
So phase diagram for this system is different (Fig 12.4)

7. Fe-C True Equilibrium Diagram
1600
1400
1200
1000
800
600
400 1 2 3 4 90 L
γ + L
 + Graphite
Liquid +
Graphite
(Fe)
C, wt% C
0.65
740°C
T(°C)
γ + Graphite
100
1153°C γ
Austenite
4.2 wt% C
α + γ
Graphite formation promoted by
__________
Cast irons have graphite
Fig. 11.2, Callister & Rethwisch 9e.
[Adapted from Binary Alloy Phase Diagrams, T. B. Massalski (Editor-in-Chief), Reprinted by permission of ASM International, Materials Park, OH.]

8. Types of Cast Iron _______ iron ___________________
Figs. 11.3(a) & (b), Callister & Rethwisch 9e. [Courtesy of C. H.
Brady and L. C. Smith,
National Bureau of
Standards, Washington,
DC (now the National
Institute of Standards
and Technology, Gaithersburg, MD]
_______ iron
___________________
weak & brittle in tension
stronger in compression
excellent _________ dampening
wear resistant
________ iron
add Mg and/or Ce
graphite as _______ not flakes
matrix often pearlite – stronger but less ductile

9. Types of Cast Iron (cont.)
Figs. 11.3(c) & (d), Callister & Rethwisch 9e.
White iron
< 1 wt% Si
pearlite + ___________
very hard and ___________
______________ iron
heat treat white iron at °C
graphite in ____________
reasonably strong and ductile
Courtesy of Amcast Industrial Corporation
Reprinted with permission of the Iron Castings Society, Des Plaines, IL

10. Types of Cast Iron (cont.)
Compacted __________ iron
relatively high _________________
good resistance to thermal shock
lower oxidation at elevated temperatures
Courtesy of Sinter-Cast, Ltd.
Fig. 11.3(e), Callister & Rethwisch 9e.

11. Production of Cast Irons
Fig.11.5, Callister & Rethwisch 9e. (Adapted from W. G. Moffatt, G. W. Pearsall, and J. Wulff, The Structure and Properties of Materials, Vol. I, Structure, p Copyright © 1964 by John Wiley & Sons, New York. Reprinted by permission of John Wiley & Sons, Inc.)

12. Limitations of Ferrous Alloys
Relatively high densities
Relatively low electrical conductivities
Generally poor corrosion resistance

13. Nonferrous Alloys NonFerrous Alloys • Cu Alloys • Al Alloys
Brass: Zn is subst. impurity
(costume jewelry, coins,
corrosion resistant)
Bronze
: Sn, Al, Si, Ni are
subst. impurities
(bushings, landing
gear)
Cu-Be :
precip. hardened
for strength
• Al Alloys
-low ρ: 2.7 g/cm3
-Cu, Mg, Si, Mn, Zn additions
-solid sol. or precip.
strengthened (struct.
aircraft parts
& packaging)
NonFerrous
Alloys
• Mg Alloys
-very low
ρ: 1.7 g/cm3
-ignites easily -
aircraft, missiles
• Ti Alloys
-relatively low ρ: 4.5 g/cm3
vs 7.9 for steel
-reactive at high T’s -
space applic.
• Refractory metals
-high melting T’s
-Nb, Mo, W, Ta
• Noble metals
-Ag, Au, Pt -
oxid./corr. resistant
Based on discussion and data provided in Section 11.3, Callister & Rethwisch 9e.

14. Metal Fabrication How do we fabricate metals? _____________________
____________ - hammer (forged)
Cast molten metal into mold
_____________________
Rough stock formed to final shape
Hot working vs Cold working
• Deformation ___________ high enough for ________________
• Large ______________
• Deformation below
_________________ temperature
• Strain hardening occurs
• Small ______________

15. Metal Fabrication Methods (i)
FORMING
CASTING
MISCELLANEOUS A o d
force
die
blank
• Forging (__________________)
(wrenches, crankshafts)
often at
elev. T
Adapted from Fig. 11.9, Callister & Rethwisch 9e.
roll A o d
• Rolling (________________)
(I-beams, rails, sheet & plate)
tensile
force A o d
die
• Drawing
(rods, wire, tubing)
die must be well lubricated & clean
ram
billet
container
force
die holder
die A o d
extrusion
• __________
(rods, tubing)
ductile metals, e.g. Cu, Al (hot)

16. Metal Fabrication Methods (ii)
FORMING
CASTING
MISCELLANEOUS
Casting- mold is filled with molten metal
_________________________, perhaps alloying elements added, then _______ in a mold
______________________________
gives good production of shapes
weaker products, internal defects

17. Metal Fabrication Methods (iii)
FORMING
CASTING
MISCELLANEOUS
• ________ Casting
(large parts, e.g.,
auto engine blocks)
What material will withstand T >1600°C and is ____________ and easy to mold?
Answer: ______!!!
To create mold, pack _____ around form (pattern) of desired shape
Sand
molten metal

18. Metal Fabrication Methods (iv)
FORMING
CASTING
MISCELLANEOUS
• _____________________
(low volume, complex shapes
e.g., jewelry, turbine blades)
Stage I — _____ formed by pouring ____________ around wax pattern Plaster allowed to harden.
wax I
• Stage II — Wax is melted and then
poured from mold—hollow mold cavity remains. II
• Stage III — __________________
into mold and allowed to solidify.
III

19. Metal Fabrication Methods (v)
FORMING
CASTING
MISCELLANEOUS
• Die Casting
-- high ____________
-- for alloys having ____ melting temperatures
• Continuous Casting
-- __________ shapes
(e.g., rectangular slabs,
cylinders)
molten
solidified

20. Metal Fabrication Methods (vi)
FORMING
CASTING
MISCELLANEOUS
• _________________
(metals w/low ductilities)
• ____________
(when fabrication of one large
part is impractical)
• Heat-affected ______:
(region in which the
microstructure has been
changed).
Fig , Callister & Rethwisch 9e.
[From Iron Castings Handbook, C.F. Walton and T.J. Opar (Ed.), Iron Castings Society,
Des Plaines, IL,1981.]
piece 1
piece 2
fused base metal
filler metal (melted)
base
metal (melted)
unaffected
heat-affected zone
pressure
heat
point contact
at low T
densification
by diffusion at
higher T
area
contact
densify

21. Thermal Processing of Metals
Annealing: Heat to Tanneal, then cool slowly.
Types of
Annealing •
Stress Relief: Reduce
stresses resulting from:
- plastic deformation
- ___________ cooling
- phase transform. •
__________
(steels):
Make very soft steels for
good machining. Heat just
below Teutectoid & hold for
15-25 h. •
Full Anneal
(steels):
Make soft steels for
good forming. Heat
to get γ
, then furnace-cool
to obtain coarse pearlite. •
_______________:
Negate effects of
cold working by
(recovery/
recrystallization) •
_________
(steels): Deform
steel with large grains. Then heat
treat to allow _______________
and formation of smaller grains.
Based on discussion in Section 11.7, Callister & Rethwisch 9e.

22. Heat Treatment Temperature-Time Pathsb)
_____________ A
_____________ P
Tempering (Tempered Martensite) B A
100%
50% 0% c)
Fig , Callister & Rethwisch 9e. [Adapted from H. Boyer (Editor), Atlas of Isothermal Transformation and Cooling Transformation Diagrams, Reproduced by permission of ASM International, Materials Park, OH.]

23. Hardenability -- Steels
• __________ – measure of the ability to form martensite
• Jominy end quench test used to measure ___________.
24°C water
specimen
(heated to γ
phase field)
flat ground
Rockwell C hardness tests
Fig , Callister & Rethwisch 9e. (Adapted from A.G. Guy, Essentials of Materials Science, McGraw-Hill Book Company, New York, 1978.)
• Plot __________ versus distance from the quenched end.
Hardness, HRC
Distance from quenched end
Fig , Callister & Rethwisch 9e.

24. Reason Why Hardness Changes with Distance
• The cooling rate _________ with distance from quenched end. 60
Martensite
Martensite + Pearlite
Fine Pearlite
Pearlite
Hardness, HRC 40 20
distance from quenched end (in) 1 2 3
600
400
200 A M P
0.1 1 10
100
1000
T(°C)
M(start)
Time (s) 0%
100%
M(finish)
Fig , Callister & Rethwisch 9e. [Adapted from H. Boyer (Ed.), Atlas of Isothermal Transformation and Cooling Transformation Diagrams, Reproduced by permission of ASM International, Materials Park, OH.]

25. Hardenability vs Alloy Composition
Cooling rate (°C/s)
Hardness, HRC 20 40 60 10 30 50
Distance from quenched end (mm) 2
100 3
4140
8640
5140
1040 80 %M
4340
• ____________ curves for
five alloys each with,
C = _____________
Fig , Callister & Rethwisch 9e. (Adapted from figure furnished courtesy Republic Steel Corporation.)
• "Alloy Steels"
(4140, 4340, 5140, 8640)
-- contain Ni, Cr, Mo
(0.2 to 2 wt%)
-- these ___________ shift
the "nose" to longer times
(from A to B)
-- martensite is easier
to form
T(°C) 10 -1 3 5
200
400
600
800
Time (s)
M(start)
M(90%) B A TE

26. Influences of Quenching Medium & Specimen Geometry
• Effect of quenching medium:
Medium
air
oil
water
Severity of Quench
_________
Hardness
_________
• Effect of specimen geometry:
When surface area-to-volume ratio increases:
-- cooling rate throughout interior increases
-- hardness throughout interior increases
Position
center
surface
Cooling rate
low
high
Hardness

27. Precipitation Hardening
• Particles impede _________ motion.
• Ex: Al-Cu system
• Procedure: 10 20 30 40 50
wt% Cu L
 + L α
α + θ θ
θ + L
300
400
500
600
700
(Al)
T(ºC)
composition range
available for precipitation hardening
CuAl2 A
-- Pt A: _______________ (get α solid solution) B
Pt B
-- Pt B: ______ to room temp. (retain α solid solution) C
-- Pt C: ________ to nucleate small θ __________ within α phase.
Other alloys that precipitation harden: • Cu-Be • Cu-Sn • Mg-Al
Fig , Callister & Rethwisch 9e. (Adapted from J.L. Murray, International Metals Review 30, p.5, Reprinted by permission of ASM International.)
Temp.
Time
Pt A (sol’n heat treat)
Pt C (precipitate )
Adapted from Fig , Callister & Rethwisch 9e.

28. Influence of Precipitation Heat Treatment on TS, %EL
• 2014 Al Alloy:
• _________ on TS curves.
• __________ T accelerates
process.
• ________ on %EL curves.
%EL (2 in sample) 10 20 30
1min 1h
1day
1mo
1yr
204ºC
149ºC
precipitation heat treat time
precipitation heat treat time
tensile strength (MPa)
200
300
400
100
1min 1h
1day
1mo
1yr
204ºC
non-equil.
solid solution
many small
precipitates
“aged”
fewer large
“overaged”
149ºC
Fig , Callister & Rethwisch 9e. [Adapted from Metals Handbook: Properties and Selection: Nonferrous Alloys and Pure Metals, Vol. 2, 9th ed., H. Baker (Managing Ed.), Reproduced by permission of ASM International, Materials Park, OH.]

29. Summary • Ferrous alloys: steels and cast irons • Non-ferrous alloys:
-- Cu, Al, Ti, and Mg alloys; refractory alloys; and noble metals.
• Metal fabrication techniques:
-- forming, casting, miscellaneous.
• Hardenability of metals
-- measure of ability of a steel to be heat treated.
-- increases with alloy content.
• Precipitation hardening
--hardening, strengthening due to formation of
precipitate particles.
--Al, Mg alloys precipitation hardenable.