Date of download: 10/17/2017 Copyright © ASME. All rights reserved. From: Microstructure and Mechanical Properties of G17CrMoV5-10 Cast Steel After Regenerative Heat Treatment J. Pressure Vessel Technol. 2010;132(6):064503-064503-5. doi:10.1115/1.4001922 Figure Legend: Influence of the phosphorus content and microstructure on the impact energy of the G17CrMoV5-10 cast steel for its long-term operation (between 50,000 and 84,000 h) at the temperature of 535°C Reprinted with permission from Stachura . Copyright ©2004, Przeglad Odlewnictwa.

Date of download: 10/17/2017 Copyright © ASME. All rights reserved. From: Microstructure and Mechanical Properties of G17CrMoV5-10 Cast Steel After Regenerative Heat Treatment J. Pressure Vessel Technol. 2010;132(6):064503-064503-5. doi:10.1115/1.4001922 Figure Legend: Influence of cooling rate on microstructure and hardness of the G17CrMoV5-10 cast steel, where F is the ferrite, B is the bainite, P is the pearlite, HV30-Vickers hardness at the load of 294 N (30 kG), V8–5-cooling rate between the temperature of 800 and 500°C