Niobium RRR and Ta specifications for SRF cavities: a critical review G. Ciovati, P. Kneisel and G. Myneni 7 th SRF Materials Workshop, July 16 th 2012.

Slides:



Advertisements
Similar presentations
The Continuing Role of SRF for AARD: Issues, Challenges and Benefits SRF performance has been rising every decade SRF installations for HEP (and other.
Advertisements

Pyrochlore Ingot Niobium SRF Technology for Next Generation Continuous Wave Accelerators Ganapati Myneni LBNL June 3, 2013.
Superconducting Materials R&D: RRCAT-JLAB Collaboration S B Roy Materials & Advanced Accelerator Science Division RRCAT, Indore Collaborators: M. K. Chattopadhyay,
Introduction to Ingot Niobium Andrew Hutton SSTIN10 Symposium Jefferson Lab Sept 22-24, 2010.
Low RRR Materials for ILC Ganapati Myneni Jefferson Lab ISOHIM & VNECA Nov 11-15, ’13 – Tokyo LCWS13, The University of Tokyo.
Presented by Grigory Eremeev Grigory Eremeev. Presented by Grigory Eremeev Outline: - Cavities and Fields; - Results; - Tricks of the Trade: new shapes;
R&D For Accelerating Structures H. Padamsee. TESLA Niobium, one meter length, rf = 1.3 GHz Copper, 53 cm, rf = 11.4 GHz.
Thin Films for Superconducting Cavities HZB. Outline Introduction to Superconducting Cavities The Quadrupole Resonator Commissioning Outlook 2.
SRF Materials R&D Alex Gurevich 1 & Pierre Bauer 2 1 Applied Superconductivity Center, UW/NHMFL 2 Fermi National Accelerator Laboratory AARD Meeting Fermilab,
Case study 5 RF cavities: superconductivity and thin films, local defect… Group A5 M. Martinello A. Mierau J. Tan J. Perez Bermejo M. Bednarek.
Cavity package T.Saeki BCD meeting 20 Dec Cavity shape BCD: TESLA shape Pros: small wakefield, HOM thoroughly investigated single-cell: 43 MV/m.
ILC PM Meeting S0 Webex Global Design Effort 1 S0/S1 Next Steps Lutz Lilje GDE.
Rong-Li Geng Jefferson Lab High Efficiency High Gradient Cavities - Toward Cutting Down ILC Dynamic Heat Load by Factor of Four R.L. Geng, ALCW2015,
Rong-Li Geng Toward Higher Gradient and Q 0 LCWS2013, U. of TokyoNov , 2013, R.L. Geng1.
Acceleration gradient limitations in room temperature and superconducting acceleration structures Nikolay Solyak Fermilab.
R EVIEW ON Q - D ROP M ECHANISM B ernard V ISENTIN International Workshop on Thin Films 9 th - 12 th October 2006.
Cavity Productions at DESY DESY -MPY- FNAL Overview on the cavity productions Review of cavity performance Some conclusions.
Deutsches Elektronen-Synchrotron Helmholtz Association of German Research Centers Hamburg, Germany Unloaded Quality Factor.
High Q R&D at JLab G. Ciovati, P. Dhakal, R. Geng, P. Kneisel, G. Myneni TTC Topical Meeting on CW SRF Cornell Univ., June 12 th -14 th, 2013.
R.L. Geng, 5/27-31,2013 ECFA LC2013, DESY 1 Update on Raising Q0 at Ultra-High Gradient via Large-Grain Niobium Material Rongli Geng Jefferson Lab ECFA.
Rongli Geng March 4, th LCC ILC Cavity Group Meeting
Q-Slope at High Gradients ( Niobium Cavities ) Review about Experiments and Explanations Bernard VISENTIN CEA - Saclay.
Group 6 / A RF Test and Properties of a Superconducting Cavity Mattia Checchin, Fabien Eozénou, Teresa Martinez de Alvaro, Szabina Mikulás, Jens Steckert.
CBMM North America – JLab CRADA Historical Remarks Ganapati Myneni Ingot Niobium Summary Workshop Jefferson Lab December 4, 2015.
Advances in Large Grain Resonators Activities of DESY, W.C. Heraeus and RI material and fabrication aspects preparation and RF test results W. Singer,
Sindhunil Barman Roy1 and Ganapati Myneni2
ANL/FNAL/UC Collaboration meeting 27 June 2008 SRF Materials: First Acceleration Test of Coated Cavities Pellin 1, Zasadzinski 2, Proslier 1,2, Norem 3,
ILC Cavity Gradient R&D Plan Proposal for Release 5 Rongli Geng for ILC Cavity Group 2jun2010 ILC SCRF WebEx Meeting 6/2/20101ILC SCRF WebEx Meeting.
Ingot Niobium Summary Workshop December 4, 2015 Jefferson Lab Swapan Chattopadhyay.
10/1/09 R.L. Geng ALCPG09, Albuquerque, NM 1 Cavity R&D Status and Future Plans - with a partial summary of SRF2009 Rongli Geng Jefferson Lab.
LHC vacuum chamber dust High Pressure pure water rinse –Developed at CERN for LEP sputtered SCRF NEG Coating –Most likely must be re-applied Nozzles and.
Advances in Development of Diffused Nb3Sn Cavities at Cornell
ALCPG2011, 3/19- 23, SRF Group Institute of Heavy Ion Physics, Peking University ALCPG /3/19-23, Eugene, Oregon, USA RF superconducting Cavity.
JLab Update Rongli Geng April 30, th LCC ILC Cavity Group Meeting.
How important is the surface finish/roughness in determining the performance of Nb cavities? Introduction Peter Kneisel Jlab.
High Temperature Heat Treatment to Raise the Quality Factor of Large Grain Niobium Cavities Pashupati Dhakal Gianluigi Ciovati Ganapati Rao Myneni July.
Annual Meeting CERN - November 2005 Bernard V ISENTIN.
Summary of the Symposium on Ingot Nb and New Results on Fundamental Studies of Large Grain Nb Gianluigi Ciovati Jefferson Lab.
Page 1 Jean Delayen Center for Accelerator Science Old Dominion University and Thomas Jefferson National Accelerator Facility SURFACE IMPEDANCE COCKCROFT.
Opportunities for ingot niobium in future accelerators Ganapati Myneni TTC Meeting, November 5-8, 2012 Jefferson Lab.
Andrew BurrillFall 2011 Project X Collaboration Meeting 650 MHz Developments at JLAB Andrew Burrill for the JLab Team.
1 SIMS Characterization of Impurity Elements in Nb: The Effect of Heat Treatments ncsu.edu/aif jlab.org 1 P. Maheshwari, F. Stevie, D. Griffis, M. Rigsbee.
Vortex hotspots in SRF cavities Alex Gurevich ODU Department of Physics, Center for Accelerator Science 7-th SRF Materials Workshop, JLab, July 16, 2012.
Raw Materials Specifications and Material Batch History (Niobium sheets used to make 9-cell cavities) Lance Cooley Head, Superconducting Materials Department,
Possible Relationship Between Defect Pre-Heating and Defect Size H. Padamsee Cornell S0 Meeting, Jan 26, 2009.
RF Superconducting Materials Workshop at Fermilab, May 23 & 24, 2007 Advanced Nb oxide surface modification by cluster ion beams Zeke Insepov, Jim Norem.
Laser heating and laser scanning microscopy of SRF cavities
High-Q, High Gradient Niobium-Coated Cavities at CERN
Surface Resistance of a bulk-like Nb Film Sarah Aull, Anne-Marie Valente-Feliciano, Tobias Junginger and Jens Knobloch.
Rongli Geng ILC Cavity Group Meeting October 25, 2011
Cavity Gradient R&D Status and Future Plans for TDP-2
Energy (ILC) and Intensity (Project X) SRF Cavity Needs
Results on second sound method
JLab infusion and LG flux expulsion update
State of the Art and Future Potential of Nb/Cu Coatings
Lance Cooley Monday morning meeting 27 September 2010
Activities of Cavity Fabrication Facility at KEK
High Q via N infusion R&D at Jefferson Lab
Material for Large Scale Cavity Production
Materials, Advanced Accelerator Science & Cryogenics Division
Effect of Surface Treatments on the Superconducting Properties of Niobium Presented by A.S.Dhavale Sept. 23, 2010.
TTC WG-2 focusing on Nb Material - Properties and Specifications -
Case study 6 Properties and test of a Superconducting RF cavity
C75 Cryomodule Project Outline
Performance of Large Grain TESLA cavities
Matthias Liepe Zachary Conway CLASSE, Cornell University June 1, 2009
LCLS-II High Q0 Cavities: Lessons Learned
Development of Large Grain Cavities at DESY
Vertical Test Results of 9-Cell Cavities for LCLS-II
JLab Work on Low Temperature Near-Surface Diffusion aka “Infusion”
Presentation transcript:

Niobium RRR and Ta specifications for SRF cavities: a critical review G. Ciovati, P. Kneisel and G. Myneni 7 th SRF Materials Workshop, July 16 th 2012 Jefferson Lab

Influence of Impurities on RRR Relationship between RRR and nonmetallic impurities measured by Tokyo Denkai Contribution of different defects in the scattering mechanism: Expected RRR contribution for Nb for 1 wt ppm of impurities

RRR and thermal conductivity Rule of thumb:  (4.2K)  0.25 W/(m K)  RRR In SRF, RRR is considered a synonymous of thermal conductivity: W. Singer, DESY BUT most bulk Nb cavities operate at 2.0 K. Phonon peak in large- grain/single-crystal material eliminates the correlation between  (2.0K) and RRR P. Dhakal, to be published

RRR and gradient: data Fine-grain, BCP vs. EP E. Kako et al., SRF’99, p GHz single- cell cavities 100  m diameter nc defect 9-cell ILC cavities H. Padamsee, “RF Superconductivity Science, Technology and Applications”, Wiley-VCH, 2009, p. 199

RRR and gradient: data W. Singer et al., Proc. of the SSTIN’10, AIP Conf. Proc. 1352, p. 13 BCP, Large-grain vs. Fine-grain

RRR and gradient: models Current and future SRF cavity applications are at f ≤ 1.5 GHz: H q independent of RRR below 2.0 K in case of defect free material G. M üller, SRF’87, p. 331

1.3 GHz, 1.8 K RRR and gradient: models Eddy current scanning can detect defects with diameter >~50  m, within ~0.5  m depth Data on RRR vs. gradient show defect size <~30  m D. Reschke, SRF’97, p. 385

RRR and R s R BCS has a minimum for surface RRR ~ GHz P. Dhakal et al., IPAC’12, paper WEPPC091 We don’t know of any correlation between RRR and RF residual resistance High RRR is not required for low R BCS

RRR and Q-slopes RRR ~ 40 E acc,quench ~ 20 MV/m P. Kneisel, JLAB-TN V. Palmieri’s model (SRF’05, p. 162): lower RRR gives higher medium field Q- slope. RRR should be at least ~100. Gurevich and Lin’s calculation [Phys. Rev. B 85, (2012)]: lower RRR (~6) gives lower medium and high field Q-slopes.

Ta in Nb: past and current specification Stanford specification: “ Since the relationship between good superconducting Nb cavity RF performance and impurity level is not experimentally demonstrated, the assumption that the Nb should be as pure as possible is made. A compromise must, however, be made between cost and impurity specifications. ” [J. P. Turneaure, Proc. of the 1972 Appl. Supercond. Conf., Annapolis, MD, pp ]. Ta was ≤ 500 wt.ppm. H. Padamsee, RF Superconductivity for Accelerators, J. Wiley & Sons, 1998, p. 106: “ Presently the ppm wt impurity level is not perceived to be a problem since tantalum is a substitutional impurity which does not substantially affect the electronic properties.” Current Ta specification: ≤ 500 wt.ppm It seems that the Ta content spec. propagated from Stanford as the “best that was commercially available”. No scientific justification was found. There was one documented case of quench at 13 MV/m in a 9-cell cavity due to Ta cluster. (W. Singer et al., SRF’97, p. 850). Rumors say that this cluster was embedded during rolling of the Nb sheets with dirty rollers

SRF cavity results 1.5 GHz single-cell study ( P. Kneisel et al., PAC’95, p ) No significant dependence of quench field on RRR B p,quench ~ 130 mT ( E acc =30.5 MV/m for ILC shape ) achieved in a cavity with 1300 wt. ppm Ta 1.3 GHz 9-cell cavity ( G. Ciovati et al., SSTIN’10, p. 25 ): B p,quench ~ 131 mT ( E acc =31 MV/m ) achieved in cavity JLab-LG1 with 1300 wt. ppm Ta (Ingot D, CBMM) Tantalum is “dissolved” in the Nb matrix

Conclusions Quality control during and post-manufacturing of Nb sheets greatly reduced the likelihood of large (> ~50  m) defects embedded in the sheets Thermal model calculations show that the quench field of defect-free Nb is independent of RRR at f ≤ 1.5 GHz and T ≤ 2.0 K Surface treatment (EP vs BCP) and metallurgy (fine-grain vs. large-grain) influence quench field as much as RRR Single and multi-cell cavities with 1300 wt.ppm Ta content achieved up to E acc ~30 MV/m The current RRR and Ta specs contribute to high cost of Nb for SRF cavities: is there enough scientific evidence to justify them?