Priplast Polyester Oligomers

Similar presentations


Presentation on theme: "Priplast Polyester Oligomers"— Presentation transcript:

1 Priplast Polyester Oligomers
Dimerized Fatty Acid Technology for Use in Epoxy Toughening

2 The Basis:Pripol Dimerized Fatty Acids
Large hydrocarbon part (C36) hydrophobic hydrolytic resistance of derivatives affinity for non-polar matrices and surfaces Irregular non-crystalline structure flexibility low Tg flow, wetting Di-functional constituent for: polyamides polyesters polyurethanes

3 Use in Epoxy resins Dimer technology traditionally used in epoxy resins In polyamide curatives In modifed epoxies Why? Brings flexibility (vibration / stress absorption) Enhances hydrophobicity, weatherability and compatibility with organic matrices (tar, hydrocarbon resins)

4 Modification of Rigid Polymers With Soft Segments
low-Tg amorphous “soft” segments 1.flexibilization crystalline or high-Tg amorphous “hard” segments soft domain, with glass transition temperature close to that of the soft segment hard domain, with melting point close to that of the rigid homopolymer

5 Modification of Rigid Polymers With Soft Segments
a bad try at flexibilization hard and soft segments are small copolymer too chopped up to form decent hard and soft domains low melting point and strength, high Tg, poor elastic recovery

6 Modification of Rigid Polymers With Soft Segments
2. impact modification crystalline or high-Tg amorphous “hard” segments low-Tg rubber balls hard, rigid, high-melting matrix with cushions to absorb impact stability of the compound is an issue

7 Dimer technology for epoxy modification
the low glass transition temperature of dimer acid makes it suitable for flexibilization and impact modification the low polarity and Tg of dimer acid is a good strating point for phase separation dimer acid itself is rather small as a soft segment (MW 580) so optimal properties cannot be reached

8 Impact Modification Technology
Polyesters based on dimerized fatty acids allow incorporation of larger mol wt soft segments, potentially resulting in better toughening performance etc. HOOC---- ----- COOH E-E n

9 Advantages of Polyester Modification Technology
HOOC---- E-E ----- COOH n Possibility to graft the soft segment on the epoxy Possibility to carefully control molecular weight and polarity To exactly establish the degree of phase separation required

10 Additional Advantages
Soft domains based on dimerized fatty acid are extremely hydrophobic, which reduces moisture diffusion through the matrix Polyesters based on dimerized fatty acids do not contain volatile toxic or smelly monomers Polyesters based on dimerized fatty acids are not susceptible to thermal or oxidative degradation Polyesters based on dimerized fatty acids have very low glass transition temperatures

11 Existing Grafted Impact Modifiers
CTBN-rubber (‘liquid rubber’) a low-MW copolymer of acrylonitrile and butadiene contains unreacted double bonds High viscosity (60000 – mPa.s at 27 ºC)

12 Test Epoxy Formulation
Heat curable formulation 72% ‘Pre-react’ dimer polyester + low mol wt BPA epoxy (‘828’ type) 15% high mol wt BPA epoxy (‘1001’ type) 4% Phenolic Novolac Catalyst Imidazole Cured at 175 C

13 Effect of Polyester Polarity
Several acid-terminated polyesters of PRIPOL 1009, low-MW dioic acid and glycol prepared Constant molecular weight Ratio of PRIPOL 1009 to low-MW dioic acid varied HUGE impact on reaction product is dimer/adipic/NPG

14 Modification with pure Pripol 1009 / glycol ester (no short-chain dioic acid)
no grafting reaction components are too incompatible polymer is brittle AND sticky

15 Modification with ester of Pripol 1009 and short dioic acid (75/25)
some grafting reaction components are still incompatible polymer is brittle AND sticky

16 Modification with ester of Pripol 1009 / short dioic acid (50/50)
full grafting reaction good phase separation on microscale polymer is hard AND tough

17 Dimer technology for epoxy toughening, dimerate vs CTBN
modifier property CTBN (1300X13) Dimerate (DA/SD/glycol) glass transition temperature (ºC) 29 22 essential work of fracture (kJ/m2) 6.5 10.5 T-peel at ambient temperature (Ga) 60 66 T-peel at ambient after 40 h / 60 ºC / 60 % RH (Ga) 57 87 Moisture Diffusivity (cm2/s) 3.0 x 10-4 0.8 x 10-4 Modifier viscosity (mPa.s)

18 Conclusions Epoxy modification with dimerized fatty acid technology allows Flexibility or toughening (even at very low temperature) Good stability against heat, oxidation and moisture (as seen in other polymer systems) A toughener which is not too high viscosity Flexibility of chemistry allows tailoring of polyester molecular weight and polarity, to fit the base epoxy resin Allows desired morphology to be exactly achieved