1
CORPORATE TRAINING AND PLANNING
INJECTION MOULDING CORPORATE TRAINING AND PLANNING
2
Historical Background
A single-action hydraulic injection machine was designed in the U.S.A. in 1870 by Hyatt Heating-cylinder design was first recognised in a patent issued to Adam Gastron in 1932. Large-scale development of injection moulding machinery design towards the machines we know today did not occur until the 1950's in Germany CORPORATE TRAINING AND PLANNING
3
Injection Moulding Process – Over View
Solid Wide neck, Flat Product is made like bucket, cabinets, Automobile & Industrial parts etc…. by injecting molten thermoplastic material in to a closed mould which is relatively cool. CORPORATE TRAINING AND PLANNING
4
Type of Injection Moulding Machine
Hand Injection Moulding M/C Plunger type Injection Moulding M/C Reciprocating Screw Type Injection Moulding M/C CORPORATE TRAINING AND PLANNING
5
CORPORATE TRAINING AND PLANNING
Hand Injection Moulding Machine vertical machine consists of Barrel, Plunger, Band Heaters along with energy regulator, Rack & Pinion system for Injecting the material by the plunger, a torpedo and nozzle. CORPORATE TRAINING AND PLANNING
6
Plunger Type Injection
Moulding Machine Vertical & Horizontal Plunger Type Injection Moulding Machine CORPORATE TRAINING AND PLANNING
7
The Reciprocating Screw
The feeding zone The compressing (or transition) zone The metering zone CORPORATE TRAINING AND PLANNING
8
CORPORATE TRAINING AND PLANNING
Machine components CORPORATE TRAINING AND PLANNING
9
CORPORATE TRAINING AND PLANNING
The Injection Process Plasticises the material by reciprocating Screw. Injects the molten material to a closed mould via a channel system of gates and runners. Cools the Mould. Refills the material for the next cycle. Ejects the Product. Closes the Mould for further cycle. CORPORATE TRAINING AND PLANNING
10
Injection Moulded Items
CORPORATE TRAINING AND PLANNING
11
Injection Moulded Items
CORPORATE TRAINING AND PLANNING
12
Injection Moulded Items
CORPORATE TRAINING AND PLANNING
13
Advantages of Injection Moulding Process
Parts can be produced at high production rates. Large volume production is possible. Relatively low labour cost per unit is obtainable. Process is highly susceptible to automation. Parts require little or no finishing. Many different surfaces, colours, and finishes are available. Good decoration is possible. For many shapes this process is the most economical way to fabricate. Process permits the manufacture of very small parts which are almost impossible to fabricate in quantities by other methods. CORPORATE TRAINING AND PLANNING
14
Advantages of Injection Moulding Process
Minimal scrap loss result as runners, gates, and rejects can be reground and reused. Same items can be moulded in different materials, without changing the machine or mould in some cases. Close dimensional tolerances can be maintained. Parts can be moulded with metallic and non-metallic inserts. Parts can be moulded in a combination of plastic and such fillers as glass, asbestos, talc and carbon. The inherent properties of the material give many advantages such as high strength-weight rates, corrosion resistance, strength and clarity. CORPORATE TRAINING AND PLANNING
15
Limitations of Injection Moulding
Intense industry competition often results in low profit margins. Mould costs are high. Moulding machinery and auxiliary equipment costs are high. Lack of knowledge about the fundamentals of the process causes problems. Lack of knowledge about the long term properties of the materials may result in long-term failures. CORPORATE TRAINING AND PLANNING
16
Machine operation sequence
The mould closes and the screw begins moving forward for injection. The cavity fills as the reciprocating screw moves forward, as a plunger. CORPORATE TRAINING AND PLANNING
17
Machine operation sequence
The cavity is packed as the screw continuously moves forward. The cavity cools as the gate freezes off and the screw begins to retract to plasticize material for the next shot. CORPORATE TRAINING AND PLANNING
18
Machine operation sequence
The mould opens for part ejection The mould closes and the next cycle begins CORPORATE TRAINING AND PLANNING
19
CORPORATE TRAINING AND PLANNING
Injection Mould CORPORATE TRAINING AND PLANNING
20
CORPORATE TRAINING AND PLANNING
Mould system A typical (three-plate) moulding system CORPORATE TRAINING AND PLANNING
21
CORPORATE TRAINING AND PLANNING
A two-plate mould. A three-plate mould. The moulded system includes a delivery system and moulded parts. CORPORATE TRAINING AND PLANNING
22
CORPORATE TRAINING AND PLANNING
Screw Used in Injection Moulding Machines The screw has three zones with a ring-plunger assembly. The Feed Zone, where the plastic first enters the screw and is conveyed along a constant root diameter; the Transition Zone, where the plastic is conveyed, compressed and melted along a root diameter that increases with a constant taper; and the Metering Zone, where the melting of the plastic is completed and the melt is conveyed forward along a constant root diameter reaching a temperature and viscosity to form parts. CORPORATE TRAINING AND PLANNING
23
CORPORATE TRAINING AND PLANNING
L/D RATIO The L/D ratio is the ratio of the flighted length (Effective Length) of the screw to its outside diameter. Most injection screws use a 20:1 L/D ratio. But it may range from 18:1 to 24:1 In the case of Thermoset it may range from 12:1 to 16:1. CORPORATE TRAINING AND PLANNING
24
High L/D Ratio results the following ….
More shear heat can be uniformly generated in the plastic without degradation; Greater the opportunity for mixing, resulting in a better homogeneity of the melt. Greater the residence time of the plastic in the barrel possibly permitting faster cycles of larger shots. CORPORATE TRAINING AND PLANNING
25
COMPRESSION RATIO (CR)
The ratio of the first flight depth of feed zone to the last flight depth of meter zone , Or, First Channel Volume of feed zone to last channel volume of metering zone, Typically ranges from 1.5:1 to 4.5:1 for most thermoplastic materials. Most injection screws classified as general purpose have a compression ratio of 2.5:1 to 3.0:1. Thermo set screws have a 1:1 ratio. CORPORATE TRAINING AND PLANNING
26
Higher the CR results the following ….
Greater shear heat imparted to the resin Greater heat uniformity of the melt High Potential for creating stresses in some resins High energy consumption CORPORATE TRAINING AND PLANNING
27
Back Pressure (Kg/Cm2 or bar)
Back pressure is the amount of pressure exerted by the material ahead of the screw, as the screw is pushed back in preparation for the next shot. Effect of Back Pressure More Homogeneous Mix Proper Melting More compact Sometime leads degradation CORPORATE TRAINING AND PLANNING
28
Injection Speed (cm/Sec)
The injection speed is the forward speed of the screw during its injection operation per unit time. Effect of Injection Speed Easy Injection of Material Avoid Short-Shot Some times leads more orientation & burn marks CORPORATE TRAINING AND PLANNING
29
CORPORATE TRAINING AND PLANNING
Screw Rotation Speed The screw rotation speed (RPM) is the rate at which the plasticizing screw rotates. The faster the screw rotation result the following .. Faster the material is compressed by the screw flights Increasing the amount of shear heating Low residence time, some less melting CORPORATE TRAINING AND PLANNING
30
CORPORATE TRAINING AND PLANNING
Cushion The cushion is the difference in the final forward position of the screw and its maximum allowable forward position. More Cushion results more residence time, some time degrades. If the screw were allowed to travel its full stroke and stop mechanically against the nozzle, the cushion would be zero. With zero Cushion no hold on works. Typically a cushion of 3 to 6 mm is used. CORPORATE TRAINING AND PLANNING
31
Materials for Injection Moulding
Acrylonitrile butadiene styrene (ABS) Acetal Acrylic Polycarbonate (PC) Polyester Polyethylene Fluoroplastic Polyimide Nylon Polyphenylene oxide Polypropylene (PP) ** Polystyrene (PS) Polysulphone Polyvinyl chloride (PVC) CORPORATE TRAINING AND PLANNING
32
CORPORATE TRAINING AND PLANNING
33
CORPORATE TRAINING AND PLANNING
Molecules lie in a definite fashion or regular arrangement CORPORATE TRAINING AND PLANNING
34
CORPORATE TRAINING AND PLANNING
35
CORPORATE TRAINING AND PLANNING
Molecules fall in Crystalline & amorphous pattern CORPORATE TRAINING AND PLANNING
36
CORPORATE TRAINING AND PLANNING
Amorphous Polymer has CORPORATE TRAINING AND PLANNING
37
CORPORATE TRAINING AND PLANNING
38
CORPORATE TRAINING AND PLANNING
While flowing in the channel or cavity of the Mould. As the melt touches the surface of the mould its viscosity increases because of lowering of melt temperature, So it slides on the Surface and the Molecules gets oriented CORPORATE TRAINING AND PLANNING
39
CORPORATE TRAINING AND PLANNING
40
CORPORATE TRAINING AND PLANNING
41
CORPORATE TRAINING AND PLANNING
42
CORPORATE TRAINING AND PLANNING
Non Newtonian Plastics CORPORATE TRAINING AND PLANNING
43
CORPORATE TRAINING AND PLANNING
Non Newtonian Plastics CORPORATE TRAINING AND PLANNING
44
CORPORATE TRAINING AND PLANNING
45
CORPORATE TRAINING AND PLANNING
Newtonian Plastic CORPORATE TRAINING AND PLANNING
46
CORPORATE TRAINING AND PLANNING
47
CORPORATE TRAINING AND PLANNING
48
CORPORATE TRAINING AND PLANNING
49
CORPORATE TRAINING AND PLANNING
50
CORPORATE TRAINING AND PLANNING
51
CORPORATE TRAINING AND PLANNING
Broad Molecular weight Distribution shows broad Melting Points CORPORATE TRAINING AND PLANNING
52
CORPORATE TRAINING AND PLANNING
Narrow Molecular weight Distribution shows sharp Melting Points CORPORATE TRAINING AND PLANNING
53
CORPORATE TRAINING AND PLANNING
Plastic Product Properties can change 10% or more by changing Process Conditions CORPORATE TRAINING AND PLANNING
54
CORPORATE TRAINING AND PLANNING
55
CORPORATE TRAINING AND PLANNING
56
CORPORATE TRAINING AND PLANNING
57
CORPORATE TRAINING AND PLANNING
58
CORPORATE TRAINING AND PLANNING
59
CORPORATE TRAINING AND PLANNING
60
CORPORATE TRAINING AND PLANNING
61
CORPORATE TRAINING AND PLANNING
62
CORPORATE TRAINING AND PLANNING
63
CORPORATE TRAINING AND PLANNING
64
CORPORATE TRAINING AND PLANNING
During Refilling CORPORATE TRAINING AND PLANNING
65
CORPORATE TRAINING AND PLANNING
During Injection CORPORATE TRAINING AND PLANNING
66
CORPORATE TRAINING AND PLANNING
67
CORPORATE TRAINING AND PLANNING
68
CORPORATE TRAINING AND PLANNING
69
CORPORATE TRAINING AND PLANNING
Additive Function Examples Filler increase bulk density calcium carbonate, talc, limestone Plasticizer improve processability, reduce product brittleness phthalate esters, phosphate esters Antioxidant prevent polymer oxidation phenols, aromatic amines Colorant provide desired part application color oil-soluble dyes, organic pigments Flame retardant reduce polymer flammability antimony trioxide Stabilizer stabilize polymer against heat or UV light carbon black, hydroxybenzophenone Reinforcement improve strength E-glass, S-glass, carbon, Kevlar fibers CORPORATE TRAINING AND PLANNING
70
CORPORATE TRAINING AND PLANNING
TOGGLE TYPE CLAMPING A toggle is mechanically device to amplify force. In a moulding machine, which consists of two bars joined, together end to end with a pivot . The end of one bar is attached to a stationary platen, and the other end of a second bar is attached to the movable platen. When the mould is open, the toggle is in the shape of a V. When pressure is applied to the pivot, the two bars form a straight line. CORPORATE TRAINING AND PLANNING
71
CORPORATE TRAINING AND PLANNING
TOGGLE TYPE CLAMPING CORPORATE TRAINING AND PLANNING
72
CORPORATE TRAINING AND PLANNING
TOGGLE TYPE CLAMPING ADVANTAGE Low cost and lower horsepower needed to run. Positive clamp of the mould DISADVANTAGE Do not read the clamp force. Clamping is more difficult. Higher maintenance as lubricant is provided. CORPORATE TRAINING AND PLANNING
73
CORPORATE TRAINING AND PLANNING
HYDRAULIC CLAMPING A clamping unit actuated by hydraulic cylinder, which is directly connected to the moving, closed the mould. In this case ram of hydraulic system is attached to moving platen. There are two halves in hydraulic cylinder, which is actually inlet and outlet of oil. When oil goes to the cylinder with pressure oil pushes the ram to forward direction by which moving platen moves and mould closed and when oil comes from the cylinder the ram come back and mould is open. CORPORATE TRAINING AND PLANNING
74
CORPORATE TRAINING AND PLANNING
HYDRAULIC CLAMPING CORPORATE TRAINING AND PLANNING
75
CORPORATE TRAINING AND PLANNING
HYDRAULIC CLAMPING ADVANTAGE Clamp speed easily controlled and stopped at any point. Direct a read out of clamp force. Easy adjustment of clamped force and easy mould set up. Low maintenance as part is self lubricated. DISADVANTAGE It is higher cost and more expensive than toggle system. None positive clamp. CORPORATE TRAINING AND PLANNING
76
CORPORATE TRAINING AND PLANNING
TIE-BAR LESS CLAMPING Tie-Bar less clamping system is basically Hydraulic clamping system without any tie bar. The platen is moved on a rail system. The main advantage of this system there is no limitation of mould platen size. As there is no tie bar so the mould dimension is not so important. Also mounting of the mould is easy and it is very useful when products eject from the mould is manual. CORPORATE TRAINING AND PLANNING
77
CORPORATE TRAINING AND PLANNING
TIE-BAR LESS CLAMPING CORPORATE TRAINING AND PLANNING
78
CORPORATE TRAINING AND PLANNING
TIE-BAR LESS CLAMPING Much larger mould mounting area. Larger stroke compared to the toggle type machines. Full machine capacity can be utilised. Smaller machines can mould larger components. Saves floor space. Saves electrical energy because of reduction in the size of machine. Has the capacity to reduce weight of the moulded component because tie-bar stretching is not there. Machine becomes very flexible for future modification. Easy access to mould cavity's because of the absence of the tie bars. Robotic arm movement becomes easy. Fewer moving parts so lesser wear and tear so longer life for machines. Lower lubrication required. Removal of mould plates much simple. Greater stability. CORPORATE TRAINING AND PLANNING
79
Theoretical Calculation
CORPORATE TRAINING AND PLANNING
80
CORPORATE TRAINING AND PLANNING
Example 1: POM has an S.G. of It is to be moulded in an Injection Moulding Machine with a shot weight of 80 gms (in PS). This machine has a shot weight of 80 x 1.42 / = gms of POM. Example 2: PP has an S.G. of It is to be moulded in an Injection Moulding Machine with a shot weight of 80 gms (in PS). This machine has a shot weight of 80 x 0.90 / 1.05 = gms of PP. CORPORATE TRAINING AND PLANNING
81
CORPORATE TRAINING AND PLANNING
Example 3: Figurines made of UPVC (S.G. 1.38) with a combined weight of figurine plus runners of 40 gms. are to be moulded. What size of machine is sufficient? Shot weight in terms of PS = 40 x 1.05/1.38 = gms. Using the 85% guide line, the machine shot weight needed = 30.43/0.85 =35.80 gms. Example 4: The same figurine in example 3 is to be moulded in a big machine. What is the biggest machine that could be used? Using the 35% rule, the biggest machine that could be used has a shot weight = 30.43/0.35 = gms. CORPORATE TRAINING AND PLANNING
82
Determining Projected Area
Projected area is calculated by multiplying length times width. CORPORATE TRAINING AND PLANNING
83
Determining Clamping Force (Tonnes)
Projected Area = Length x Width and multiplying that area by a clamp factor of between 2 and 8. Most commonly factor 5 is used. Clamp Force = Projected Area x 5 For every inch of depth the clamp force must be increased by 10%. CORPORATE TRAINING AND PLANNING
84
CORPORATE TRAINING AND PLANNING
Example 5: What is the residence time of UPVC (S.G. 1.38) in a machine with screw diameter of 55 mm, injection stroke of 250 mm, shot weight (PS) of 567 g, and a cycle time of 10 s moulding shots weighing 260 g? Volume of melt in the barrel is estimated to be two times the injection volume = 2 * * 5.5 * 5.5 * 25 / 4 = 1188 cm3 Barrel residence time = 1188 * 1.38 * 10 / 260 = 63 s Example 6: A GPPS cup of diameter 79 mm is to be moulded. The cup is 0.6 mm at its thinnest section. Find a conservative clamping force which would be sufficient. The projected area of the cup (and runner) is * 7.92 / 4 = 49 cm2. This cup belongs to the thin wall domain. The conservative clamping force is 0.62 * 49 = 30.4 tonnes. CORPORATE TRAINING AND PLANNING
85
CORPORATE TRAINING AND PLANNING
Example 7: The same GPPS cup has a flow path length of 104 mm. Find a more accurate clamping force needed. Flow path to thickness ratio (L/T Ratio) = 104 / 0.6 = 173. From Figure 2, at 0.6 mm wall thickness, the cavity pressure is 550 bar. 1 bar = 1.02 kg/cm2. The clamping force = 550 * 1.02 * 49 = 27,500 kg = 27.5 tonnes. The above calculation has not accounted for viscosity. It turns out to be still correct as the viscosity factor for GPPS is 1.0. Example 8: The same cup as in the above example is to be made out of ABS. Find the clamping force needed. Using the viscosity factor of 1.5, the clamping force needed = 1.5 * 27.5 tonnes = 41.3 tonnes. CORPORATE TRAINING AND PLANNING
86
CORPORATE TRAINING AND PLANNING
Plastic flow Simple shear flow. Simple extensional flow. (c) Shear flow in cavity filling. (d) Extensional flow in cavity filling. CORPORATE TRAINING AND PLANNING
87
CORPORATE TRAINING AND PLANNING
where CORPORATE TRAINING AND PLANNING
88
CORPORATE TRAINING AND PLANNING
When Plastics flow in the cavity, the pressure decreases along the delivery system and the cavity CORPORATE TRAINING AND PLANNING
89
CORPORATE TRAINING AND PLANNING
Injection pressure as a function of melt viscosity, flow length, volumetric flow rate, and part thickness CORPORATE TRAINING AND PLANNING
90
Setting Machine Process Conditions
1 Set the melt temperature 2 Set the mold temperature 3 Set the switch-over position 4 Set the screw rotation speed 5 Set the back pressure 6 Set the injection pressure to the machine maximum 7 Set the holding pressure at 0 MPa 8 Set the injection velocity to the machine maximum 9 Set the holding time 10 Set ample remaining cooling time CORPORATE TRAINING AND PLANNING
91
Setting Machine Process Conditions
11 Set the mold open time 12 Mold a short-shot series by increasing injection volume 13 Switch to automatic operation 14 Set the mold opening stroke 15 Set the ejector stroke, start position, and velocity 16 Set the injection volume to 99% mold filled 17 Increase the holding pressure in steps 18 Minimize the holding time 19 Minimize the remaining cooling time CORPORATE TRAINING AND PLANNING
92
Basic Process Factors in Injection Moulding
Material Parameters Amorphous, Semicrystalline, Blends and Filled Systems Pressure-Volume-Temperature (PVT) Behaviour Viscosity Geometry Parameters Wall Thickness of Part Number of Gates Gate Location Gate Thickness and Area Type of Gates: Manually or Automatically Trimmed Constraints from Ribs, Bosses and Inserts Manufacturing Parameters Fill Time Packing Pressure Level Mold Temperature Melt Temperature CORPORATE TRAINING AND PLANNING
93
CORPORATE TRAINING AND PLANNING
Residual stress The development of residual flow stresses due to frozen-in molecular orientation during the filling and packing stages. (1) High cooling, shear, and orientation zone (2) Low cooling, shear, and orientation zone CORPORATE TRAINING AND PLANNING
94
CORPORATE TRAINING AND PLANNING
95
CORPORATE TRAINING AND PLANNING
Process Controls Injection Moulding cycle can be broken down into four phases: Fill, Pack, Hold, and Cooling/plastication These phases can be controlled by following variables: Injection Speed, Plastic Temperature, Plastic Pressure, Cooling Temperature and Time. CORPORATE TRAINING AND PLANNING
96
CORPORATE TRAINING AND PLANNING
97
CORPORATE TRAINING AND PLANNING
98
CORPORATE TRAINING AND PLANNING
Cycle time in injection moulding CORPORATE TRAINING AND PLANNING
99
CORPORATE TRAINING AND PLANNING
100
Post Moulding Operation
Heat inserting Chrome Plating In Mould Insert Moulding Post Mould Inserting Drilling Polishing Assembly CORPORATE TRAINING AND PLANNING
101
CORPORATE TRAINING AND PLANNING
Secondary operations Bonding Welding Inserting Staking Swaging Assembling with fasteners CORPORATE TRAINING AND PLANNING
102
CORPORATE TRAINING AND PLANNING
Secondary operations Appliqué: a surface covering applied by heat and pressure Printing: a process of making a mark or impression onto a substrate for decorative or informational purposes. Painting Hard coating Metallizing/shielding Surface treatment Annealing Machining CORPORATE TRAINING AND PLANNING
103
Benefits of Post Moulding Operations
Reduced costs – by carrying out post moulding operations in house, and utilising lean manufacturing tools, we can greatly reduce component costs and the complexity of work that our customers would ordinarily undertake. High level of quality – performing post-moulding operations on products helps ensure that a high level of quality is maintained. By checking parts from the moment they leave a press, to final assembly, quality levels can be maintained and ensure that components are only assembled to the highest standards. Reduction of Customer’s stock holding – Assembly of components will reduce the cost of customers stock holding due to delivery of an assembly rather than a range of components. Reduced production times – post moulding operations mean there is very little time between the production of components and their assembly. This means that a great deal of time can be saved when components would normally be transported, or stored, in between moulding and assembly operations. CORPORATE TRAINING AND PLANNING
104
CORPORATE TRAINING AND PLANNING
Heat inserting is the addition of inserts into a part increases the functionality of a part by which components can be assembled. CORPORATE TRAINING AND PLANNING
105
Benefits of Heat Inserting
Increased functionality – by adding inserts to mouldings the part can more easily be used for its designed purpose. For example by adding threaded inserts parts can be easily be screwed to their fixings or other parts, increasing their functionality. Low part degradation – the process of heat inserting means that the heating/melting of the part is very localised to where the insert will be pressed in. this means that parts do not suffer warping, or any other distortion effects, due to being heated again. High level of quality – due to the known challenges with heat inserting extra measures are taken to ensure the processes is repeated to as high a level as possible, meaning part quality is kept very high. CORPORATE TRAINING AND PLANNING
106
CORPORATE TRAINING AND PLANNING
Chrome Plating Due to the chrome plating process requiring the part to be electrically conductive, a series of steps are required before the chrome can be deposited onto the surface of the product. CORPORATE TRAINING AND PLANNING
107
Benefits of Chrome Plating
Metal finish - Metal finishes can be very popular and, by coating plastics, advantage can be taken of characteristics from both materials. Wear resistant – as chrome is a metal rather than a plastic its wear resistance properties are much greater than those of the plastic it covers. This means for applications where a part might be handled repeatedly, such as a shower handset, a chrome finish is likely to wear better than its plastic counterpart. Electrically conductive parts – by chrome or nickel plating a part it is possible to give a plastic component the ability to conduct electricity. This gives the advantage of being able to create electrical components that are light weight and less costly to produce than completely metal parts. Attractive mouldings – by applying chrome finish to mouldings a CORPORATE TRAINING AND PLANNING
108
CORPORATE TRAINING AND PLANNING
In Mould Insert Moulding In mould insert moulding is the process by which a metal, or preformed plastic, insert is incorporated in to the component during the moulding stage. CORPORATE TRAINING AND PLANNING
109
Benefits Of In Mould Insert Moulding
Reduced post-moulding operations – With in mould insert moulding the need for post moulding operations is greatly reduced. This helps with ease of assembly and reduces the labour necessary for products. Increased part consistency – Insert Moulding has major benefits in the consistency of parts produced. As the inserts are placed in the same locations in tools for every cycle each of the mouldings produced will be exactly the same. This helps reduce costs, as rejected parts will be kept to a minimum. Ease of assembly – Due to inserts being incorporated into parts during the moulding stage this eases the assembly of the part. Instead of having to place fittings to attach parts fittings can be incorporated during the moulding stage so that parts can be simply clipped together. Reduced production time – when vertical moulding machines, that are equipped with a rotary table, are used for production there is the opportunity to have two halves of the lower part of the tool. This means that production is almost constant with mouldings being formed at the same time as fresh inserts are being loaded into the second half of the tool. This lowers overall production times and can also reduce the amount of labour needed. CORPORATE TRAINING AND PLANNING
110
CORPORATE TRAINING AND PLANNING
Post Mould Inserting Post mould inserting is the process by which a metal, or preformed plastic, insert is incorporated into a moulding by means of a secondary process once the component has already been moulded. CORPORATE TRAINING AND PLANNING
111
Benefits of Post Mould Inserting
Ease of assembly – by adding inserts to a moulding the ease by which it can be assembled is greatly increased. Inserts such as clips or screw bolts can be incorporated into mouldings which greatly assist assembly operations and subsequent product performance. Increased part functionality – besides adding inserts to aid assembly inserts that improve a parts functionality can also be used. For example, terminal fittings for wires, or seals to make parts watertight. Increased component value – any second operation carried out on a part will add value to it. By adding inserts to help assembly or increase functionality, product value will be raised. This helps to compensate for the extra time involved in second operations and ensure products remain cost effective. Good part consistency – to carry out post mould inserting jigs are used to hold mouldings while they are inserted. This means that the repeatability of the operation is very good and all parts inserted will be of the same quality. CORPORATE TRAINING AND PLANNING
112
CORPORATE TRAINING AND PLANNING
Drilling The drilling of parts is used to remove any unnecessary polymer that may have been necessary in the moulding process. By removing this extra material in house it means a ready-to-assemble moulding can be provided to the customer, or the part can be assembled with other mouldings. CORPORATE TRAINING AND PLANNING
113
CORPORATE TRAINING AND PLANNING
Polishing For products that have a high quality gloss finish a post moulding polishing operation is often a useful extra process. Even though the finish produced by the moulding tool may be of a very high quality, a polishing operation to remove any dust from the product before final packaging gives a part the high gloss finish that will have been specified.. Polishing operations are carried out on a soft-polishing wheel with high quality wax to ensure that a part is polished to a perfect finish without leaving any marks. CORPORATE TRAINING AND PLANNING
114
CORPORATE TRAINING AND PLANNING
Assembly For products that require assembly we are able to carry out this operation in our assembly facility. We can demonstrate examples of assemblies where we mould all the separate components in house and assemble the parts either as a whole in the assembly facility or as a step by step process on the press as each part is produced. By carrying out assembly in house we can reduce costs for our customers while still producing products to a high standard. CORPORATE TRAINING AND PLANNING
115
CORPORATE TRAINING AND PLANNING
Faults & Remedies CORPORATE TRAINING AND PLANNING
116
CORPORATE TRAINING AND PLANNING
Sink Marks Depression in a moulded part caused by shrinking or collapsing of the resin during cooling. CORPORATE TRAINING AND PLANNING
117
CORPORATE TRAINING AND PLANNING
Sink Marks - Problems Resin feed inadequate Improper mould design. Parts cool too rapidly Rib section in part too wide. Temperature of mould surface opposite rib too hot. Entrapped gas. Nozzle too restrictive, land length too long. Pressure too low. Mould temperature too low or high Stock temperature too high Gate too small Improper gate location Nozzle and metering zone temperatures too high. Excessive cooling time in mould Unbalanced flow pattern. Bad check valve. CORPORATE TRAINING AND PLANNING
118
CORPORATE TRAINING AND PLANNING
Jetting Turbulence in the resin melt flow caused by undersized gate, abrupt change in cavity volume, or too high injection pressure. CORPORATE TRAINING AND PLANNING
119
CORPORATE TRAINING AND PLANNING
Jetting - Problems Excessive injection speed. Melt temperature too high. Melt temperature too low. mould Temperature too low. Nozzle opening too small. Gate and length too long. Sprue, runner, and/or gate size too small. Nozzle heating band malfunction. Inefficient gate location. CORPORATE TRAINING AND PLANNING
120
Splay Marks (Silver Streaking, Splash Marks)
Marks or droplet type imperfections formed on the surface of a finished part. CORPORATE TRAINING AND PLANNING
121
Splay Marks (Silver Streaking, Splash Marks) - Problems
Obstruction in nozzle. Screw rpm too high. Back pressure too low. Melt temperature too high. Nozzle too hot. Nozzle too small. Gates too small. Sprue too small. Insufficient venting. Burr in runner or gate. Cracked mould. Trapped volatiles. Excessive moisture. Resin contaminated. mould cavity contamination. Excessive shot size. CORPORATE TRAINING AND PLANNING
122
CORPORATE TRAINING AND PLANNING
Blush Discoloration generally appearing at gates, around inserts, or other obstructions along the flow path. Usually indicates weak points. CORPORATE TRAINING AND PLANNING
123
CORPORATE TRAINING AND PLANNING
Blush - Problems mould temperature too cold Injection fill speed too fast Melt stock temperature too high or too low. Improper gate location Sprue and nozzle diameter too small. Nozzle temperature too low. Insufficient cold slug well. Sharp Corners in gate area Resin excessively moist. Inadequate injection pressure. CORPORATE TRAINING AND PLANNING
124
CORPORATE TRAINING AND PLANNING
Burn Marks Black marks or scorch marks on surface moulded part; usually on the side of the part opposite the gate or in a deep cavity. CORPORATE TRAINING AND PLANNING
125
CORPORATE TRAINING AND PLANNING
Burn Marks - Problems Excessive Injection speed Excessive injection pressure. Inefficient mould temperature. Excessive amount of volatiles due to improper Venting. Improper gate location Front zone temperature too high. Screw speed too high. Excessive back pressure. Compression ratio of screw too high. Faulty temperature controllers. Frictional burring--gates too small Dead material hung up on screw or nozzle. Melt stock temperature too high or too low. Nozzle diameter too small Over-heated heater band Incorrect screw rpm. CORPORATE TRAINING AND PLANNING
126
Poor Weld Lines (Knit Lines)
Inability of two melt fronts to knit together in a homogeneous fashion during the moulding process, resulting in weak areas in the part of varying severity. CORPORATE TRAINING AND PLANNING
127
Poor Weld Lines - Problems
Material too cold. Injection speed too slow Entrapment of air at weld line. Improper mould design. Contamination of poorly dispersed pigments. Core shifting. mould temperature to low. Injection speed too slow. Melt stock temperature to low. Injection pressure too low. Insufficient mould venting Cylinder temperature too low. Injection back pressure too low. Nozzle diameter too small. Excessive screw flights in metering zone. Improper gate locations and/or size. Distance from gate excessive. Ineffective flow pattern. mould release agent (brittle weld lines). Inadequate flow. CORPORATE TRAINING AND PLANNING
128
CORPORATE TRAINING AND PLANNING
Voids (Bubbles) An unfilled space of such size that it scatters radiant energy such as light. CORPORATE TRAINING AND PLANNING
129
CORPORATE TRAINING AND PLANNING
Voids - Problems Injection pressure too low Packing time too short Insufficient feed of material mould temperature too low. Injection speed too high Excessive cushion At the side of a rib; rib too thick. Runners or gate too small or badly positioned. CORPORATE TRAINING AND PLANNING
130
Delamination (Skinning)
Surface of the finished part separates or appears to be composed of layer of solidified resin. Strata or fish scale type appearance where the layers may be separated. CORPORATE TRAINING AND PLANNING
131
Delamination - Problems
Contamination of resin by additives or other foreign materials. Resin temperature too low. Non-uniformity of resin temperature. Wrong mould temperature. Excessive material moisture. Inadequate injection speed. Sharp corners at gate. Incompatible polymers. CORPORATE TRAINING AND PLANNING
132
CORPORATE TRAINING AND PLANNING
Flow Lines and Folds Mark visible on the finished item that indicate the direction of flow in the cavity. CORPORATE TRAINING AND PLANNING
133
Flow Lines and Folds - Problems
Stock temperature too low. Runners too small Improper gate size and/or location. mould temperature too low. Inadequate cold slug well. CORPORATE TRAINING AND PLANNING
134
Excessive Warpage/ Shrinkage
Excessive dimensional change in a part after processing, or the excessive decrease in dimension in a part through cooling. CORPORATE TRAINING AND PLANNING
135
Warpage / Shrinkage -Problems
mould closed time too short. Inefficient injection forward time. Ram speed too high or too low. Injection and holding pressure too high or low. Melt temperature inadequate. Excessive nozzle and metering zone temperatures. mould temperature too high (for thick wall sections). Parts cool unevenly. Parts underpacked. Improper gate location. Gate too restrictive Unequal temperature between mould halves. Non-uniform part ejection. Parts mishandled after ejection. Unbalanced gates on multiple gated part. Too many stresses in part. CORPORATE TRAINING AND PLANNING
136
CORPORATE TRAINING AND PLANNING
Black Specks Particles in the surface of an opaque part and visible throughout a transparent part. CORPORATE TRAINING AND PLANNING
137
Black Specks - Problems
Contamination of material. Holdup of molten resin moulding machine or mould runner system. Press Contamination. Local over-heating in the injection cylinder. Defective closure of the nozzle. Oxidation by occluded air or inadequate air venting mould contains grease. Trapped air Inefficient injection speed. CORPORATE TRAINING AND PLANNING
138
CORPORATE TRAINING AND PLANNING
Brittleness Tendency of a moulded part to break, crack, shatter, etc. under conditions which it would not normally do so. CORPORATE TRAINING AND PLANNING
139
Brittleness - Problems
mould temperature too high Inadequate cooling in gate area Gate section of item too thin (gate brittleness) Resin too cold. Non-uniformity of resin temperature. Undried material. Contamination. Poor part design. Material degraded. Non-compatible mould release. Packing the mould. Melt temperature too cold. Excessive amounts of regrind. CORPORATE TRAINING AND PLANNING
140
Brittleness - Problems
Inadequate mould temperature Excessive screw rpm Excessive back pressure Insufficient venting. Improper gate location. Excessive injection speed. Excessive residence timed Melt temperature too high. Nozzle too hot. Injection pressure too low (weld lines). Runners and gates in adequate (weld lines). Dwell time in the injection cylinder too long (material degraded). Material degraded during drying or pre-heating CORPORATE TRAINING AND PLANNING
141
CORPORATE TRAINING AND PLANNING
Flash Excess plastic around the area of the mould parting line on a moulded part. CORPORATE TRAINING AND PLANNING
142
CORPORATE TRAINING AND PLANNING
Flash - Problems mould parting surfaces do not seal properly. Injection pressure too high. Clamp pressure set too low or projected area or item too large for clamp pressure of the machine. Injection temperature too high. Feed needs adjustment. Hold time too long. Inadequate mould supports. Oversize vents. CORPORATE TRAINING AND PLANNING
143
CORPORATE TRAINING AND PLANNING
Blister Defect on the surface of a moulded part caused by gases trapped within the part during curing. CORPORATE TRAINING AND PLANNING
144
CORPORATE TRAINING AND PLANNING
Blister - Problems Screw rpm too high Back pressure too low mould temperature too low. Gate improperly located Insufficient venting. Regrind too coarse CORPORATE TRAINING AND PLANNING
145
CORPORATE TRAINING AND PLANNING
Crazing Fine cracks in part surface. May extend in a network over the surface or through the part. CORPORATE TRAINING AND PLANNING
146
CORPORATE TRAINING AND PLANNING
Crazing - Problems Insufficient drying of the material. Contamination. Injection temperature too high (crazing accompanied by dis-coloring or yellowing). mould surface contaminated Inadequate injection speed. Inefficient injection forward time. Excessive injection pressure. mould temperature too low. Gate too large. CORPORATE TRAINING AND PLANNING
147
CORPORATE TRAINING AND PLANNING
Cracking Fracture of the plastic material in an area around a boss, projection, or moulded insert. CORPORATE TRAINING AND PLANNING
148
CORPORATE TRAINING AND PLANNING
Cracking - Problems Parts cool too quickly moulded-in stress Wall thickness too heavy for compound. CORPORATE TRAINING AND PLANNING
149
CORPORATE TRAINING AND PLANNING
Low Gloss Surface roughness resulting from high speed fill which causes surface wrinkling as the polymer melt flows along the wall of the mould. CORPORATE TRAINING AND PLANNING
150
CORPORATE TRAINING AND PLANNING
Low Gloss - Problems Inadequate polish of mould surface. Material or mould too cold. Air entrapment. Melt index of material too low. Improper mould design. Wrong injection pressure. Excessive injection speed. CORPORATE TRAINING AND PLANNING
151
CORPORATE TRAINING AND PLANNING
Low Gloss - Problems Inadequate flow. Contamination Resin excessively moist Sprue, runners, and/or gate size too small. Pigment agglomerates. Oil or grease on knockout pins. CORPORATE TRAINING AND PLANNING
152
Injection of insufficient material to fill the mould.
Short Shot Injection of insufficient material to fill the mould. CORPORATE TRAINING AND PLANNING
153
CORPORATE TRAINING AND PLANNING
Short Shot - Problems Insufficient feed, cushion. Inadequate injection pressure. Inadequate injection speed. Insufficient booster or injection high-pressure time. Inefficient screw delay. Inadequate injection back pressure. Melt temperature too low. Cylinder temperature inadequate. mould temperature too low. CORPORATE TRAINING AND PLANNING
154
CORPORATE TRAINING AND PLANNING
Short Shot - Problems Gates, sprues, and/or runners too small. Excessive screw flights in metering zone. Insufficient venting. Improper gate location. Melt index of resin too low. Excessive clearance between non-return valve and barrel. Screw bridging. Injection press of insufficient capacity. CORPORATE TRAINING AND PLANNING
155
CORPORATE TRAINING AND PLANNING
THANK YOU CORPORATE TRAINING AND PLANNING