F. Borgnolutti June 10 th, 2013 Layer jump: Only hard way bent design

2
Conductor Properties – version 1 11/15/2012F. Borgnolutti Reacted bare conductor UnitOLD (Frascati)New Width mm18.63818.513 Thickness inmm1.4621.505 Thickness outmm1.6731.682 Mid-thicknessmm1.5681.594 Keystone angledeg0.650.55 Insulation thickness0.150mm 2 Un-reacted bare conductor UnitOLD (Frascati)New Widthmm18.150 Mid-thicknessmm1.525 Keystone angledeg0.650.55 Thickness inmm1.438 Thickness outmm1.612 2 % growth in width 4.5 % growth in thickness

3
Only hard-way bend ramp 11/15/2012F. Borgnolutti3 Matlab model of the coil to see if there are solutions that gives good field quality with the constraint of a layer jump with hard way bend only:

4
Only hard-way bend ramp 11/15/2012F. Borgnolutti4 teta alpha

5
Only hard-way bend ramp 11/15/2012F. Borgnolutti5 Matlab model of the coil to see if there are solutions that gives good field quality with the constraint of a layer jump with hard way bend only:

6
Only hard-way bend ramp 11/15/2012F. Borgnolutti6 Matlab model of the coil to see if there are solutions that gives good field quality with the constraint of a layer jump with hard way bend only: b6 b10 b14

7
Conductor Properties 11/15/2012F. Borgnolutti PIT/RRP (Paolo’s parametrization) 45% copper : 2450 A/mm 2 @ 12 T, 4.2K 632 A 1400 A/mm 2 @ 15 T, 4.2 K 361 A 5% degradation Self field correction (Peak field taken at r= 0.85×r wire ) 0.454 T/kA (r=0.85*rwire) 7 Strand RRP (Arno’s parametrization) 47% copper 2650 A/mm 2 @ 12 T, 4.2K 706 A 1400 A/mm 2 @ 15 T, 4.2 K 373 A 5% degradation Self field correction: (straight wire, Peak field taken at r= 0.89×r wire ) 0.529 T/kA (r=0.89*rwire) 0.554 T/kA (r=0.85*rwire) Specification critical current Degradation and self field correction

8
Conductor Properties 11/15/2012F. Borgnolutti8 Arno’s parametrization available on plone: https://plone.uslarp.org/MagnetRD/DesignStudies/QX-CD/ShortSample/

Similar presentations

OK

Development of the EuCARD Nb 3 Sn Dipole Magnet FRESCA2 P. Ferracin, M. Devaux, M. Durante, P. Fazilleau, P. Fessia, P. Manil, A. Milanese, J. E. Munoz.

Development of the EuCARD Nb 3 Sn Dipole Magnet FRESCA2 P. Ferracin, M. Devaux, M. Durante, P. Fazilleau, P. Fessia, P. Manil, A. Milanese, J. E. Munoz.

© 2017 SlidePlayer.com Inc.

All rights reserved.

Ads by Google

Ppt on education system in india during british rule Ppt on fact and opinion Ppt on fast food business Ppt on indian water purifier industry Ppt on gender inequality in india Download ppt on threaded binary tree Ppt on diode family Ppt on digital image processing using matlab Ppt on pf and esi act Ppt on balanced diet and nutrition