CERN- Bonding A.Pezous CERN, 13.03.2013. Copyright 2013 CSEM | Bonding| A.Pezous | Page 1 Design 2 NA62 frame 2 ATLAS 8 explosions 10 micro-chevron.

Similar presentations


Presentation on theme: "CERN- Bonding A.Pezous CERN, 13.03.2013. Copyright 2013 CSEM | Bonding| A.Pezous | Page 1 Design 2 NA62 frame 2 ATLAS 8 explosions 10 micro-chevron."— Presentation transcript:

1 CERN- Bonding A.Pezous CERN,

2 Copyright 2013 CSEM | Bonding| A.Pezous | Page 1 Design 2 NA62 frame 2 ATLAS 8 explosions 10 micro-chevron

3 Copyright 2013 CSEM | Bonding| A.Pezous | Page 2 Process flow Split 1Split 2Split 3Split 4 Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) SiO2 etch - BHF Surface activation Bonding Bake 1050°C Frontside lithographie INLET-OUTLET opening DRIE etching (Si-186um) Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) KOH SiO2 etch-BHF Surface activation Bonding Bake 1050°C Frontside lithographie INLET-OUTLET opening DRIE etching(Si-186um) Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) Backside lithographie INLET-OUTLET opening DRIE etching KOH SiO2 etch-BHF Surface activation Bonding Bake 1050°C Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) Backside lithographie INLET-OUTLET opening DRIE etching KOH SiO2 etch-BHF Surface activation Bonding Bake 400°C, 12h #3#5#7, #8#9

4 Copyright 2013 CSEM | Bonding| A.Pezous | Page 3 Results- after etching

5 Copyright 2013 CSEM | Bonding| A.Pezous | Page 4 #3-split 1(no KOH) Avant recuit Après recuit Split 1 Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) SiO2 etch - BHF Surface activation Bonding Bake 1050°C Frontside lithographie INLET-OUTLET opening DRIE etching (Si-186um) #3

6 Copyright 2013 CSEM | Bonding| A.Pezous | Page 5 Avant recuit Après recuit #5- split2: KOH Split 2 Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) KOH SiO2 etch-BHF Surface activation Bonding Bake 1050°C Frontside lithographie INLET-OUTLET opening DRIE etching(Si-186um) #5

7 Copyright 2013 CSEM | Bonding| A.Pezous | Page 6 Avant recuit Après recuit #8-split3: ouverture avant bonding Split 3 Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) Backside lithographie INLET-OUTLET opening DRIE etching KOH SiO2 etch-BHF Surface activation Bonding Bake 1050°C #7, #8

8 Copyright 2013 CSEM | Bonding| A.Pezous | Page 7 #9-split4: ouverture avant bonding et LTFB Split 4 Wetox 1um Backside lithographie « alignement cross » DRIE etching SiO2(1um)+Si (2um) Frontside lithographie « channels » DRIE etching SiO2(1um)+Si(194 um) Backside lithographie INLET-OUTLET opening DRIE etching KOH SiO2 etch-BHF Surface activation Bonding Bake 400°C, 12h #9

9 Copyright 2013 CSEM | Bonding| A.Pezous | Page 8 #4- cross-section Après Après amincissement

10 Thank you for your attention!


Download ppt "CERN- Bonding A.Pezous CERN, 13.03.2013. Copyright 2013 CSEM | Bonding| A.Pezous | Page 1 Design 2 NA62 frame 2 ATLAS 8 explosions 10 micro-chevron."