www.ldc-brushplating.com2 LDC borstplätering www.ldc-brushplating.com3 LDC Portable Electroplating 1.Cold process: used at room temperature, no stress.

Similar presentations


Presentation on theme: "www.ldc-brushplating.com2 LDC borstplätering www.ldc-brushplating.com3 LDC Portable Electroplating 1.Cold process: used at room temperature, no stress."— Presentation transcript:

1

2 www.ldc-brushplating.com2 LDC borstplätering

3 www.ldc-brushplating.com3 LDC Portable Electroplating 1.Cold process: used at room temperature, no stress or adjustments because of termal distorsion. 2.To tolerance: normaly no machining required 3.Quick metal build-up: 0,05 mm in 10-15 min. 4.Plating: on all conductive materials, cast iron, stainless, mild steel, copper, chrome etc 5.Dense deposits: no or very little porosity in most coatings 6.Many differens metals: nickel, gold, silver, copper, cobolt, zinc and alloys. 7.Excellent bonding: molecular bonding results in very god adhesion, all coatings can be machined, ground or polished. 8.Mobile equipment: the repair can be done on site

4 www.ldc-brushplating.com4 Retainingrings, part of generator for powerstation, silverplated. LDC borstplätering

5 www.ldc-brushplating.com5 Retainingrings, part of generator for powerstation, silverplated. LDC borstplätering

6 www.ldc-brushplating.com6 Bus bar, contact rods for the power generating industry, gold and silver coated contact-surfaces for increased conductivity. LDC borstplätering

7 www.ldc-brushplating.com7 On-site plating job, shafts to be restored LDC borstplätering

8 www.ldc-brushplating.com8 Electric rotor with bad / worn bearing / seal areas repaired to original size. LDC borstplätering

9 www.ldc-brushplating.com9 Electric rotor with bad / worn bearing / seal areas repaired to original size. LDC borstplätering

10 www.ldc-brushplating.com10 Endcover of cast iron or Aluminium with worn /mismachined bearing seat corrected by LDC nickel. LDC borstplätering

11 www.ldc-brushplating.com11 Worn shaft on a turbine wing in power plant, to be repaired. LDC borstplätering

12 www.ldc-brushplating.com 15 LDC borstplätering Tel: +46 248 17440 ldc@swipnet.se Onsite repair of 2 pieces of seal surfaces on a compressor shaft due to local wear damage. Built with the LDC- 2904 Copper Hi- speed 0.5 mm.

13 www.ldc-brushplating.com 16 LDC borstplätering Tel: +46 248 17440 ldc@swipnet.se Finished compressor shaft to its original dimensions, with a hard, dense top layer of the LDC- 2874 Nickel Tungsten. With a hardness of 58 Hrc

14 www.ldc-brushplating.com14 LDC borstplätering Highly polished cylinders with damages is corrected by LDC plating Bearing journals and sealareas can be repaired on a Turboshaft

15 www.ldc-brushplating.com15 LDC borstplätering Propellershaft sleeve repaired on-site in England by LDC

16 www.ldc-brushplating.com16 Documented view of enlarged LDC- 2807 Nickel layer, as part of quality control. LDC borstplätering

17 www.ldc-brushplating.com17 Typical document of approval for LDC in Sweden. LDC borstplätering


Download ppt "www.ldc-brushplating.com2 LDC borstplätering www.ldc-brushplating.com3 LDC Portable Electroplating 1.Cold process: used at room temperature, no stress."

Similar presentations


Ads by Google