Extraction of iron and steel Final Form  Molten steel to final form  Molten steel to Ingots to desired shape.

Similar presentations


Presentation on theme: "Extraction of iron and steel Final Form  Molten steel to final form  Molten steel to Ingots to desired shape."— Presentation transcript:

1 Extraction of iron and steel Final Form  Molten steel to final form  Molten steel to Ingots to desired shape

2 Extraction of iron and steel Molten steel to direct final form  Coarsely Crystalline  Relatively brittle and weak

3 Extraction of iron and steel 1.Molten steel to Ingots 2.Ingots to desired shape Process Involved is rolling with heat treatment Improvement of properties Ductility Crystalline structure

4 Extraction of iron and steel Rolling

5 Extraction of iron and steel 1.Molten steel to Ingots 2.Ingots to desired shape Process Involved is forging Close small cavities Reduce the grain size Increase the density of the steel

6 Forging of steel Shaping the metal using compressive stresses

7 Extraction of iron and steel 1.Molten steel to Ingots 2.Ingots to desired shape Process Cold working : Any plastic deformation below the lowest critical temperature Introduction of Strain hardening Significant increase in tensile strength Significant decrease in ductility

8 Extraction of iron and steel Heat treatment for improvement of properties  Annealing  Hardening  Tempering

9 Annealing Process: 1.Heating at 800 o C 2.Maintaining heat at 800 o C 3.Gradual cooling Benefits 1.Production of softness 2.Relieving of internal strains 3.Refinement of the grain size 4.Weaker but ductile steel 5.Tougher

10 Annealing Process: 1.Heating at 800 o C 2.Maintaining heat at 800 o C 3.Rapid cooling Benefits 1.Normalized 2.Relieving of internal strains 3.Refinement of the grain size

11 Hardening Cooling by sudden immersion in quenching medium like 1.Oil 2.Water 3.Brine Due to quenching steel becomes brittle

12 Tempering Reheating at 200 to 500 o C Lower than preliminary heating Slow or rapid cooling Also know as drawing operation 1.Steel becomes softer 2.Steel becomes ductile 3.Tougher than all others